High entropy alloys (HEAs) are a relatively new class of solid solution alloys that contain multiple principal elements to take advantage of their high configurational entropy, sluggish diffusion, lattice distortion, and the cocktail effect. In recent development, work hardening mechanisms known as twinning induced plasticity (TWIP) and transformation induced plasticity (TRIP) have been found active in Al0.3CoCrFeNi (molar fraction) and Fe50Mn30Co10Cr10 (at %) HEA compositions. Friction-stir processing was done to increase the mechanical properties and improve the microstructure of the alloys for the purpose of high strain rate performance. Quasi-static tensile tests as well as top-hat geometry Split-Hopkinson pressure bar tests were conducted to view the mechanical properties as well as view the microstructural evolution at dynamic strain rates. Overall, the Al0.3CoCrFeNi condition after friction-stir processing and heat treatment has proved to have the best mechanical properties, and selecting from the conditions in this study, Al0.3CoCrFeNi has better shear localization resistance.
Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc1538737 |
Date | 08 1900 |
Creators | Macdonald, Neil |
Contributors | Mishra, Rajiv, Mukherjee, Sundeep, Williams, Jim |
Publisher | University of North Texas |
Source Sets | University of North Texas |
Language | English |
Detected Language | English |
Type | Thesis or Dissertation |
Format | viii, 42 pages, Text |
Rights | Use restricted to UNT Community, Macdonald, Neil, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |
Page generated in 0.0153 seconds