Effects Of Retempering With Superplasticizer On Properties Of Prolonged Mixed Mineral Admixture Containing Concrete At Hot Weather Conditions

Concrete which is manufactured in a mixing plant to be delivered to construction site in unhardened and plastic stage is called ready-mixed concrete. Because of technical and economical reasons, many mineral and chemical admixtures are used in ready-mixed concrete production.

As a result of extra mixing and delayed placing of ready-mixed concrete (especially at hot weather conditions), there can be many problems about concrete, like slump loss.

Addition of water for retempering concrete is the usual procedure, but addition of water without proper adjustment in mixture proportions, adversely affects compressive strength.

During this study, effects of prolonged mixing and retempering with superplasticizer on properties of fresh and hardened concrete at hot weather conditions are observed. Some of the properties of concrete inspected are compressive strength, splitting tensile strength, slump and air content. All mixes contain air entrainer and water reducer at a standard amount. The difference between mixes comes from kind and amount of mineral admixture which cement is replaced by. During the study, fly ash, blast furnace slag, ground clay brick and natural pozzolan are used at amounts, 25% and 50% of cement. Also, a mixture of pure cement is prepared as control concrete.

15 cm initial slump is planned in the experimental work. After five minutes and at the end of first, second, third and fourth hours of mixing process, if needed retempering process is proceeded with superplasticizer and samples are taken. As a result of retempering with superplasticizer, the aimed slump values are obtained. The effects are than, observed.

As a result of this study, it has been observed that replacing Portland cement with certain mineral admixtures, especially fly ash at certain amounts, can be a solution for slump loss problem, by retarding the slump loss effect of prolonged mixing. Also it has been seen that ground clay brick causes better performance for slump values at lateral stages of mixing with respect to pure Portland cement. Another important observation has been about the increase in the amount of air caused by air entraining admixtures in fresh concrete based on prolonged mixing at hot weather conditions.

Identiferoai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/3/12606751/index.pdf
Date01 November 2005
CreatorsYazan, Kazim
ContributorsTuranli, Lutfullah
PublisherMETU
Source SetsMiddle East Technical Univ.
LanguageEnglish
Detected LanguageEnglish
TypeM.S. Thesis
Formattext/pdf
RightsTo liberate the content for public access

Page generated in 0.0021 seconds