Bulk magnesium materials produced nowadays via powder metallurgy are based on a vastly extensive technological spectrum, which makes it possible to create a wide range of materials. This work focuses on the preparation of bulk materials from magnesium powder by cold pressing and hot pressing, sintering and field assisted sintering. The bulk materials were prepared in a series of compacting pressures from 100 MPa to 500 MPa and the sintering temperatures were selected in the range of 300 ° C to 600 ° C in order to characterize the influence of the manufacturing conditions and technology on the final properties of bulk materials. Prepared materials were evaluated in terms of microstructure, hardness, microhardness, three-point bend test, and fractography. From the hot pressed materials, the samples prepared at 400 and 500 MPa and 400 °C had the highest strength and hardness. The classic sintering of magnesium in the furnace with argon atmosphere proved to be ineffective due to the oxide layer on the surface and the presence of oxygen in technical argon. The SPS sintering (Spark Plasma Sintering) was the more effective with the lower applying pressure used to make the preforms and with the higher applied pressure during the SPS process itself. Highest strength and hardness were achieved in this case of materials sintered at 600 ° C prepared from free powder and the most porous preform (100 MPa). The bulk materials were prepared using all methods used, but the properties of these materials varied considerably depending on the technology used.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:390297 |
| Date | January 2018 |
| Creators | Březina, Matěj |
| Contributors | Pacal, Bohumil, Vojtěch, Dalibor, Ptáček, Petr |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0025 seconds