An Investigation of Bent-Beam Stress-Corrosion Test for Titanium Alloys

Titanium alloys are highly resistant to all types of corrosion due to their excellent ability to form an oxide film on the surface. However, under certain circumstances, these alloys may experience an environmental degradation which could potentially, under the application of mechanical stress, lead to a complete failure of the material. One of these cracking processes is stress-corrosion cracking (SCC). SCC has an embrittling effect on otherwise ductile materials under tensile stress. Since titanium alloys are frequently used in the aerospace industry and it is therefore of interest to test these alloys in different environment in order to prevent any future accidents. SCC testing is frequently tested at GKN Aerospace and a new testing method is of interest. The main objective with this work was to gain knowledge of the testing method. Bent-beam testing method has been used to investigate stress-corrosion cracking (SCC) of titanium alloys in a laboratory based experiment. The bent-beam testing method was of type 2-point bent beam test, where a saline solution was applied at the apex of the specimen. The specimens were loaded to a range of stresses from 40%, to 95% of the materials yield strength and the salt concentration in the saline solution was 1wt% and 3wt%. By doing so, a relative susceptibility of the different alloys could be established. Three different titanium alloys were tested: Ti-6Al-4V, Ti-8Al-1Mo-1V, and Ti-6Al-2Sn-4Zr-2Mo. The testing method was able to cause cracking on all titanium alloys, where Ti-6Al-4V was found to be the least susceptible to SCC. Ti-8Al-1Mo-1V, and Ti-6Al-2Sn-4Zr-2Mo showed an overall high susceptibility to SCC as cracking occurred in all testing configurations. Cracking was observed on both the surface of the specimen as well as in the cross sections, where the cracks grew perpendicular to the surface. SEM was also used to evaluate the crack propagation in Ti-8Al-1Mo-1V, and Ti-6Al-2Sn-4Zr-2Mo, and it was found that the cracks grew mostly along the grain boundaries.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:ltu-75212
Date January 2019
CreatorsLeón Zapata, Daniel
PublisherLuleå tekniska universitet, Institutionen för teknikvetenskap och matematik
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.002 seconds