In well cementing, the cement slurry is exposed to the conditions far different than those of ordinary Portland cement (PC) used in construction. After placement, hardened cement paste should preserve integrity and provide zonal isolation through the life of the well. American Petroleum Institute (API) Class G cement is the most common cement type used in various well conditions. Class G cement has a high degree of sulfate resistance which makes it more stable than PC when subjected to the compulsive well conditions. Ground granulated blast furnace slag (GGBFS) blended cement has a long history of use in the construction industry, but is not extensively used in well cementing applications.
This study presents an experimental program to investigate the applicability of CEM I and GGBFS blended cement pastes in the well cementing industry. Class G cement and blends of CEM I and GGBFS with the proportions (80:20), (60:40), (40:60) and (20:80) are prepared with same water/cement ratio (0.44) as restricted for Class G cement in API Specification 10A to be tested. The cement pastes are cured for ages of 1 day, 7 days and 28 days at 80
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12614683/index.pdf |
| Date | 01 September 2012 |
| Creators | Alp, Baris |
| Contributors | Yaman, Ozgur Ismail |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | Access forbidden for 1 year |
Page generated in 0.0024 seconds