The aim of my diploma thesis was to explore the influence of manganese ions put into nickel nitrate structure. The attention was focused mainly on the stabilization of nickel nitrate a modification, which could not change into b modification. The theoretical part of my thesis focused on applied materials, kinds of acumulators, basic parameters of acumulators and the description of chosen methods of measurement employed. It contained the electrodeposition, the impedance spectroscopy and the cyclic voltammetry. The task of the experimental part was to measure the effect of manganese ions put into potassium hydroxide structure. Proportions of Ni (nickel nitrate) : Mn (manganese nitrate) 10:0, 7:3, 5:5, 6:1 and 6:4 were blended for the measurement. By means of the electrodeposition, there was a thin layer of nickel hydroxide with an admixture of manganese ions from nickel nitrate and manganese nitrate dilution put on the nickel plate. After the spread of the thin layer on the nickel plate, the measurement by the method of cyclic voltammetry followed. The next task consisted in trying to add KOH (potassium hydroxide) anionic and cationic surfactant into the dilution.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:218706 |
Date | January 2010 |
Creators | Cirkovský, Jaroslav |
Contributors | Vrbický, Jiří, Sedlaříková, Marie |
Publisher | Vysoké učení technické v Brně. Fakulta elektrotechniky a komunikačních technologií |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0014 seconds