In a 6-week rat model it was demonstrated that a small dose of peri-implant zoledronic acid (ZA) increased local bone formation 3-fold compared with controls. Ancillary in vitro studies using 14C-labeled ZA implant doses demonstrated biphasic elution profiles for implants coated with hydroxyapatite; complete ZA release occurred within one to three weeks in serum compared with only 60% ZA release after 12 weeks in water. Implants without hydroxyapatite coating showed more burst-type release profiles and full ZA elution within 24 hours of hydration in serum or water. Canine studies at 6 weeks using implants with 14C-labeled ZA showed that the compound remained localized, with the greatest ZA concentration immediately adjacent to the implant. Although there was evidence of skeletal ZA distribution via diffusion into the circulation, the levels were two orders of magnitude less than at the implant site.
Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:QMM.112582 |
Date | January 2008 |
Creators | Roberts, Jacintha. |
Publisher | McGill University |
Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
Language | English |
Detected Language | English |
Type | Electronic Thesis or Dissertation |
Format | application/pdf |
Coverage | Master of Engineering (Department of Biomedical Engineering Dept.) |
Rights | All items in eScholarship@McGill are protected by copyright with all rights reserved unless otherwise indicated. |
Relation | alephsysno: 002731711, proquestno: AAIMR51473, Theses scanned by UMI/ProQuest. |
Page generated in 0.0021 seconds