Chemistry of intermetallic bonded diamond is studied. The impact resistance and energies of intermetallic bonded diamond is compared to current poly crystalline diamond compacts. IBD’s are found to have high standards of hardness and have more impact energies absorbed. Intermetallic bonded diamond composite comprises of diamond particles dispersed in Tungsten carbide using Nickel aluminide (Ni3Al) as binder. In previous research conducted on IBD’s, diamonds are successfully dispersed in intermetallic alloy of nickel aluminide and processed at 1350°C such that diamond particles remain intact without forming graphite. Composites are formed by milling, pressing the intermetallic binder and diamond particles and sintering at high temperature conditions.
| Identifer | oai:union.ndltd.org:siu.edu/oai:opensiuc.lib.siu.edu:theses-3005 |
| Date | 01 August 2016 |
| Creators | Gorla, Sai prasanth |
| Publisher | OpenSIUC |
| Source Sets | Southern Illinois University Carbondale |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses |
Page generated in 0.0024 seconds