Análise de corrosão e fratura de implantes/componentes protéticos de titânio comercialmente puro, após serem submetidos a ciclos de fadiga em um meio fluoretado com diferentes Ph

Made available in DSpace on 2014-06-11T19:28:03Z (GMT). No. of bitstreams: 0
Previous issue date: 2006Bitstream added on 2014-06-13T18:57:07Z : No. of bitstreams: 1
sartori_r_me_arafo.pdf: 1051874 bytes, checksum: cefcb24c1a056b34cdd58078fbe9390f (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Universidade Estadual Paulista (UNESP) / Atualmente o titânio é empregado como biomaterial devido sua biocompatibilidade e resistência à corrosão, entretanto os íons fluoretos são efetivos no processo de corrosão. O objetivo deste estudo foi analisar a influência de um meio fluoretado com diferentes pH nas propriedades mecânicas e na resistência à corrosão dos conjuntos implantes/componentes protéticos à base de Ti c.p., a partir dos testes de ciclagem mecânica, microscopia eletrônica de varredura (MEV) e dureza. Foram simulados cinco anos de uso regular de meios de higiene oral com conteúdo de 1500 ppm de NaF, com dois diferentes pH, mediante imersão das amostras nesse meio durante 184 horas. As amostras foram testadas num durômetro Micromet 2001. Os dados dos testes de dureza foram analisados pelo teste de Wilcoxon, demonstrando que as amostras sofreram influência negativa na dureza após a ação dos íons fluoreto. Entretanto, essa influência não ocorreu nos testes de ciclagem mecânica realizados em uma máquina de ensaios universais MTS-810, fixada a 100.000 ciclos, 15Hz e programada com força de fadiga a 150 N. Pela análise de MEV e EDS não foi contatado evidências de corrosão na superfície das amostras após ação de íons fluoretos, nem incorporação de íons fluoretos sobre a superfície dos conjuntos. Concluiu-se que a concentração de flúor e o pH das soluções não exerceram influência nas propriedades mecânicas e na resistência à corrosão. / Titanium has been widely used as biomaterial owing to its excellent corrosion resistance, mechanical properties and biocompatibility. However, it has been reported that fluoride-containing environments can attack titanium. The aim of this study was evaluated fluoride environments influence with different pH values in the implant/abutment sets. The implants were separated into 3 groups containing 7 implants/brand: one was submerged in acid fluoride environment (NaF 1500ppm 184h pH 5.3), one in neutral fluoride environment (NaF 1500ppm 184h pH 7.4), and other group in distillated water, simulating five years of dental hygiene. Hardness and surface texture were evaluated before and after fluoride exposition by Vickers method (500gf 30s) and scanning electron microscopy (SEM), respectively. The fatigue test was performed with 100.000 load cycles, 15 Hz and 150 N. There was decrease in hardness in implants submitted to the fluoride environment. SEM and EDS evaluation showed dark stains in all implants, irrespective of fluoride pH, resulting from pitting corrosion process. All sets supported the fatigue test until 100.000 load cycles. The results demonstrated that fluoride environment there was no influence in mechanical properties and corrosion resistence of the implant/abutment sets.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/96206
Date January 2006
CreatorsSartori, Rafael [UNESP]
ContributorsUniversidade Estadual Paulista (UNESP), Vaz, Luis Geraldo [UNESP], Marcantonio Junior, Elcio [UNESP]
PublisherUniversidade Estadual Paulista (UNESP)
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format79 p. : il.
SourceAleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP
Rightsinfo:eu-repo/semantics/openAccess
Relation-1, -1, -1

Page generated in 0.0019 seconds