White Light Emitting Diodes of Non-fully Conjugated Coil-like Polymer Doped with Derivatized Multi-wall Carbon Nanotubes

Luminescent emission of non-fully conjugated homopolymers was successfully demonstrated as light emitting diodes (LEDs) in this research. Coil-like heterocyclic aromatic poly[2,2-(2,5-dialkyloxyphenylene)-4-4¡¦-hexafluoroisopropanebibenzoxazo- les] (6F-PBO-CnOTpA, with n = 10, 15, and 20) was synthesized, and polymer composites of 6F-PBO-CnOTpA was in-situ synthesized with acidified multi-wall carbon nanotube (MWNT- COOH).
The non-fully conjugated coil-like heterocyclic aromatic homopolymer was synthesized by reacting 2,2,bis-(3-amino-4-hydroxy[henyl]-hexafluoropropane with 2,5-dialkyloxyterephthalic acid (CnOTpA) for 6F-PBO-CnOTpA, with n = 10, 15, and 20. In addition, MWNT was acidified for connecting the carboxylic group (-COOH) to reduce its aspect ratio and entropy induced aggregation. MWNT-COOH was analyzed using elemental analysis (EA) and viscometry to validate the effects of acidification period. The EA result seemed to suggest that the oxygen content increased, and the carbon and the hydrogen contents decreased with acidification period. The inherent viscosity (£binh) decreased according to acidification period suggesting that the aspect ratio was indeed decreased.
A hole transport layer of PEDOT¡GPSS was applied for multi-layer LEDs,. The LEDs all showed a threshold voltage about 4 V also for the composites of 6F-PBO-CnOTpA in-situ polymerized with MWNT-COOH. The 6F-PBO-CnOTpA LEDs with and without MWNT-COOH showed an electroluminescence emission range of 400 to 750 nm.

Identiferoai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0728106-122233
Date28 July 2006
CreatorsChang, Yi-jyun
ContributorsJin-long Hong, Jui-hung Hsu, Ming Chen, Shih-jung Bai
PublisherNSYSU
Source SetsNSYSU Electronic Thesis and Dissertation Archive
LanguageCholon
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0728106-122233
Rightsnot_available, Copyright information available at source archive

Page generated in 0.002 seconds