Previous issue date: 2018-01-30 / A moldagem por injeção é um dos processos mais versáteis e amplamente empregada na manufatura de polímeros. Entretanto, há uma incidência de tantos fatores que tendem a influenciar o processo, ao ponto que um controle rigoroso dos parâmetros do processo se faz necessário para obtenção de peças com nível de qualidade adequada. Neste estudo, foram avaliadas as relações entre condições de processo, microestrutura e propriedades para o polímero Acrilonitrila-Butadieno-Estireno (ABS). Para tal, o ABS foi injetado em 9 condições, variando-se importantes parâmetros de injeção: temperatura do fundido (entre 210 e 240 ºC), temperatura do molde (45 – 65 ºC), pressão de compactação (150 - 250 bar) e velocidade de injeção (50 – 110 cm3/s). A partir dos resultados das propriedades mecânicas obtidas (Resistência sob Tração, Resistência ao Impacto, Módulo Elástico e Força Máxima sob Impacto), foram desenvolvidos 3 modelos de predição, determinados via Método Taguchi, Superfície de Resposta e Regressão Linear, sendo que o Método Taguchi apresentou maior eficácia. A partir dos modelos de previsão foram escolhidas 4 condições de injeção distintas da matriz ortogonal, no intuito de se verificar a precisão dos modelos criados. A microestrutura foi avaliada através da Microscopia Eletrônica de Varredura (MEV) de amostras fraturadas por impacto instrumentado e pela medição dos domínios elastoméricos (distribuição do tamanho do Polibutadieno) via análise de imagem. Por fim, foi aplicado o tratamento térmico de alívio de tensões, as propriedades mecânicas foram determinadas e por fim comparadas entre presença e ausência de tratamento térmico, onde foi observado que não se apresentou efeito considerável. / Injection molding is one of the most versatile and widely used processes in the manufacture of polymers. However, there is an incidence of so many factors that tend to influence the process, to the point that strict control of the process parameters is necessary to obtain pieces with adequate quality level. In this study, the relationships between process conditions, microstructure and properties for acrylonitrile-butadiene-styrene (ABS) polymer were evaluated. To do this, ABS was injected under 9 conditions, varying important injection parameters: melt temperature (between 210 and 240 ºC), mold temperature (45-65 ºC), compression pressure (150-250 bar) and injection rate (50-110 cm 3 / s). From the results of the mechanical properties obtained (Resistance under Traction, Impact Resistance, Elastic Modulus and Maximum Force under Impact), 3 prediction models were developed, determined by the Taguchi Method, Response Surface and Linear Regression, with the Taguchi Method was more effective. From the prediction models four different injection conditions of the orthogonal matrix were chosen, in order to verify the accuracy of the models created. The microstructure was evaluated by Scanning Electron Microscopy (SEM) of fractured samples by instrumented impact and by the measurement of the elastomeric domains (distribution of the polybutadiene size) through image analysis. Finally, the thermal treatment of stress relief was applied, the mechanical properties were determined and finally compared between the presence and absence of heat treatment, where it was observed that no considerable effect was observed.
Identifer | oai:union.ndltd.org:IBICT/oai:tede2.uepg.br:prefix/2564 |
Date | 30 January 2018 |
Creators | Cordova, Bruno Alexandro Bewzenko |
Contributors | Carvalho, Benjamin de Melo, Pinheiro, Luís Antônio, Lucas, Alessandra de Almeida |
Publisher | Universidade Estadual de Ponta Grossa, Programa de Pós-Graduação em Engenharia e Ciências de Materiais, UEPG, Brasil, Departamento de Engenharia de Materiais |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Biblioteca Digital de Teses e Dissertações da UEPG, instname:Universidade Estadual de Ponta Grossa, instacron:UEPG |
Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0015 seconds