abstract: In this study, the stereolithography (SLA) 3D printing method is used to manufacture honeycomb-shaped flat sorbents that can capture CO2 from the air. The 3D-printed sorbents were synthesized using polyvinyl alcohol (PVA), propylene glycol, photopolymer resin, and an ion exchange resin (IER). The one-factor-at-a-time (OFAT) design-of-experiment approach was employed to determine the best combination ratio of materials to achieve high moisture swing and a good turnout of printed sorbents. The maximum load limit of the liquid photopolymer resin to enable printability of sorbents was found to be 44%. A series of moisture swing experiments was conducted to investigate the adsorption and desorption performance of the 3D-printed sorbents and compare them with the performance of IER samples prepared by a conventional approach. Results from these experiments conducted indicate that the printed sorbents showed less CO2 adsorptive characteristics compared to the conventional IER sample. It is proposed for future research that a liquid photopolymer resin made up of an IER be synthesized in order to improve the CO2-capturing ability of manufactured sorbents. / Dissertation/Thesis / Masters Thesis Mechanical Engineering 2020
| Identifer | oai:union.ndltd.org:asu.edu/item:57325 |
| Date | January 2020 |
| Contributors | Obeng-Ampomah, Terry (Author), Phelan, Patrick (Advisor), Lackner, Klaus (Committee member), Shuaib, Abdelrahman (Committee member), Arizona State University (Publisher) |
| Source Sets | Arizona State University |
| Language | English |
| Detected Language | English |
| Type | Masters Thesis |
| Format | 60 pages |
| Rights | http://rightsstatements.org/vocab/InC/1.0/ |
Page generated in 0.0022 seconds