Low-dielectric (k) films are one of the performance drivers for continued scaling of integrated circuit devices. These films are needed in microelectronic device interconnects to lower power consumption and minimize cross talk between metal lines that "interconnect" transistors. Low-k materials currently in production for the 45 and 65 nm node are most often organosilicate glasses (OSG) with dielectric constants near 2.8 and nominal porosities of 8-10%. The next generation of low-k materials will require k values 2.6 and below for the 45 nm device generation and beyond. The continuous decrease in device dimensions in ultra large scale integrated (ULSI) circuits have brought about the replacement of the silicon dioxide interconnect dielectric (ILD), which has a dielectric constant (k) of approximately 4.1, with low dielectric constant materials. Lowering the dielectric constant reduces the propagation delays, RC constant (R = the resistance of the metal lines; C = the line capacitance), and metal cross-talk between wires. In order to reduce the RC constants, a number of low-k materials have been studied for use as intermetal dielectrics. The k values of these dielectric materials can be lowered by replacing oxide films with carbon-based polymer films, incorporating hydrocarbon functional groups into oxide films (SiOCH films), or introducing porogens in the film during processing to create pores. However, additional integration issues such as damage to these materials caused by plasma etch, plasma ash, and wet etch processes are yet to be overcome. This dissertation reports the effects of plasma, temperature and chemical reactions on low-k SiOCH films. Plasma ash processes have been known to cause hydrophobic films to lose their hydrophobic methyl groups, rendering them to be hydrophilic. This allows the films to readily absorb moisture. Supercritical carbon dioxide (SC-CO2) can be used to transport silylating agents, hexamethyldisilazane (HMDS) and diethoxy-dimethlysilane (DEDMS), to functionalize the damaged surfaces of the ash-damaged films. The thermal stability of the low-k films after SC-CO2 treatment is also discussed by performing in-situ heat treatments on the films. UV curing has been shown to reduce the amount of pores while showing only a limited change dielectric constant. This work goes on to describe the effect of UV curing on low-k films after exposing the films to supercritical carbon dioxide (CO2) in combination with tetramethylorthosilicate (TMOS).
Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc33192 |
Date | 12 1900 |
Creators | Osei-Yiadom, Eric |
Contributors | Reidy, Richard F., Du, Jincheng, Scharf, Thomas W., Banerjee, Rajarshi |
Publisher | University of North Texas |
Source Sets | University of North Texas |
Language | English |
Detected Language | English |
Type | Thesis or Dissertation |
Format | xiv, 171 p. : ill., Text |
Rights | Public, Copyright, Osei-Yiadom, Eric, Copyright is held by the author, unless otherwise noted. All rights reserved. |