Solution density modelling is important in hydrometallurgical processes as accurate predictions of single and mixed electrolytes can be used in the design of equipment and their sizing, heat transfer calculations and choosing of materials for construction.
This research project entails modeling of electrolyte solutions by extending the Laliberte and Cooper (compound level) model to ionic level where an electrolyte solution is modeled as a mixture of cations, anions and water molecules. This modeling predicts single and mixed electrolyte density as a function of electrolyte temperature in degrees Celsius; water, cation and anion apparent volumes in cubic centimeters; and their respective concentrations in the electrolyte as mass fractions.
The model was developed by fitting single electrolyte density data reported in literature using the least squares method in Microsoft Excel®. The following 26 single electrolyte solutions were used in the fitting exercise: Al2(SO4)3, BaCl2, CaCl2, CdSO4, CoCl2, CuSO4, FeCl3, FeSO4, HCl, HCN, HNO3, K2CO3, LiCl, MgSO4, MnCl2, Na2SO3, NaF, NaI, NaOH, (NH4)2SO4, NiCl2, SrCl2, ZnCl2, ZnBr2, (NH4)2C2O4 and KNO2. The above electrolytes attributed to the following ions: Al3+, Ba2+, Ca2+ Cd2+, Co2+, Cu2+, Fe3+, Fe2+, H+1, K+1, Li+1, Mg2+, Mn+2, Na+1, NH4+1, Ni2+, Sr+2, Zn2+, SO42-, Cl-1, CN-1, NO3-1, CO32-, OH-1, SO32-, Br-1, F-1, I-1, C2O4-2 and NO2-1. This translated to a combination of at least 216 single electrolyte solutions which could be feasibly modeled, and a solution with at most 10 anions for mixed electrolytes, which is comparable with practical hydrometallurgical solutions.
A database of volumetric parameters was generated comprising a total of 18 cations and 12 anions. The validation of the developed model was done by predicting densities for both single and mixed electrolytes not used in the fitting exercise. The average density error i.e. the difference between experimental and model density for the single electrolyte solutions was 22.62 kg m-3 with a standard deviation of 39.66 kg m-3. For the mixed electrolytes, the average density error was 12.34 kg m-3 with a standard deviation of 24.48 kg m-3. These calculated errors translated to a maximum percentage average error of less than 4% for single electrolyte solutions and maximum average percentage of less than 3% for mixed electrolyte solutions.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:wits/oai:wiredspace.wits.ac.za:10539/16726 |
| Date | 23 January 2015 |
| Creators | Chagonda, Trevor |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis |
| Format | application/pdf, application/pdf |
Page generated in 0.0017 seconds