The work is focused on evaluation of factors influencing behaviour of interface in low toughness ceramic materials reinforced with fibres. The main aim was to characterise processing effects influencing the quality of fibre-matrix interface, with respect to final behaviour of composites at various loading type. The partial goal was to map the possibility of influencing the composite material by choice of matrix material, eventually by change of its processing, leading to change of interfacial properties without need of modification of reinforcement surface. The materials used in studied composites as a matrix were based on thermal transformation of polymer precursors, thus, the resulting materials were characterised in partially as well as in fully pyrolyzed state. Behaviour of interface in cpomposite materials was first evaluated from the global behaviour (i.e., change of mechanical properties) and in chosen representative composites also from the point of local changes in close surrounding of the interface (i.e., microstructure, chemical processes, fracture-mechanic processes, etc.) due to thermal exposition. In experiment were used particularly composite materials prepared by pyrolysis of polysiloxane resins reinforced by basalt fibres or Nextel™720 fibres. With respect to thermal resistance of the reinforcement, the basalt reinforced composites contained only partially pyrolyzed matrix (i.e., to temperature of 800°C), and in composites with Nextel™720 reinforcement was the matrix in form of fully pyrolyzed polymer into ceramic (SiOC). At partial pyrolysis of polysiloxane resin occurs rapid change of behaviour at temperature of 600°C. It was demonstrated, that around this temperature the formed interface with basalt fibre exhibits optimum adhesion/strength, allowing to reach sufficient level of composite strength at acceptable fracture toughness. Above temperature of 750°C occur significant difusion processes in the area of the interface and formation of new crystalline phases in the fibre, what deteriorates the fibre strength, and on the contrary, strengthen the interface cohesion, what leads to degradation of properties of the whole composite. At composite materials determined for high temperatures, reinforced by Nextel™720 fibres, was detected significant resistivity against oxidation caused especially by fully pyrolyzed matrix. As similarly important factor was observed the formation of mullite interphase in surface area of the fibre. Volume changes caused by formation of the interphase, difusional transport of the matter and thermal exposition led to formation of thermally and stress-induced micro-cracks, weakening interfacial surrounding in matrix as well as in fibre. This mechanism in contrast to amplifying chemical bond between fibre and matrix led to preserving of the composite properties also at high temperatures up to 1500°C. The work also dealed with effects of loading rate, where in contrast to static loading were observed different failure mechanisms. Realized research led to description and explanation of the influence of the fibre-matrix interface by change of matrix material processing parameters, which allow processing of economically advantageous and thermally stable composite.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:354849 |
| Creators | Halasová, Martina |
| Contributors | Chlup, Zdeněk |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0016 seconds