This diploma thesis focuses on the resistance of concrete to abrasion with regard to the raw materials used for their production. In the theoretical part of the thesis are described admixtures, different types of aggregate and aggregate composition which influence the resistance of concrete to abrasion. In the experimental part, 15 different C30 / 37, S4 concrete formulations were proposed. Different types of aggregates - fecal gravel (Žabčice), biotic granodiorite (Olbramovice) and amphibolite (Želešice) have always been used in the recipes. Fine ground limestone, micro-silica, high-temperature fly ash and finely ground slag were ingredients that were added to the proposed recipes. Consistency was determined by the method of cone seating and the density of fresh concrete. In the hardened state, concrete density, compressive strength, bending tensile strength, tensile strength, watertightness, concrete absorption, and abrasion resistance were determined using the Böhm method and wide wheel method. The test specimens were tested after 7, 28, and 90 days of maturation.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:392338 |
Date | January 2019 |
Creators | Černá, Hana |
Contributors | Novosad, Petr, Bodnárová, Lenka |
Publisher | Vysoké učení technické v Brně. Fakulta stavební |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0019 seconds