Nerve autografts are widely used clinically to repair nerve grafts. However, nerve grafts have many limitations, such as, availability of donor nerve grafts, and loss of function at donor site. To overcome these problems, we have used a tissue engineering approach to design three-dimensional (3D) agarose scaffolds containing gradients of laminin-1 (LN-1) and nerve growth factor (NGF) to mimic in vivo conditions to promote nerve regeneration in rats.
To determine the effect of LN-1 gradients on neurite extension in vitro, dorsal root ganglia (DRG) from chick embryos were cultured in 3D hydrogels. A gradient of LN-1 molecules in agarose gels was made by diffusion technique. LN-1 was then immobilized to the agarose hydrogels using a photo-crosslinker, Sulfo-SANPAH (Sulfosuccinimidyl-6-[4-azido-2-nitrophenylamino] hexanoate). Anisotropic scaffolds with three different slopes of LN-1 gradients were used. Isotropic scaffolds with uniform concentrations of LN-1, at various levels, were used as a positive control. DRG cultured in anisotropic scaffolds with optimal slope of LN-1 gradient extended neurites twice as fast as DRG in optimal concentration in isotropic scaffolds. Also, in the anisotropic scaffolds the faster growing neurites were aligned along the direction of LN-1 gradient.
To promote nerve regeneration in vivo, tubular polysulfone guidance channels containing agarose hydrogels with gradients of LN-1 and NGF (anisotropic scaffolds) were used to bridge 20-mm nerve gaps in rats. Nerve autografts were used as positive controls and isotropic scaffolds, with uniform concentration of LN-1 and NGF, were used as negative controls. After 4-months, the rats were sacrificed and nerve histology was done to test for nerve regeneration. Only anisotropic scaffolds and nerve autografts contained evidence of axonal regeneration. Both groups had similar numbers of myelinated axons and similar axonal-diameter distribution. However, nerve graft group performed better in functional outcome as measured by relative gastrocnemius muscle weight (RGMW) and electrophysiology. Optimization of performance of anisotropic scaffolds by varying the LN-1 and NGF concentration gradients might lead to development of scaffolds that can perform as well as nerve auotgrafts for nerve regeneration over long nerve gaps.
Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/14504 |
Date | 09 April 2007 |
Creators | Dodla, Mahesh Chandra |
Publisher | Georgia Institute of Technology |
Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
Detected Language | English |
Type | Dissertation |
Page generated in 0.0018 seconds