We investigate the conditions under which electron irradiation of single-walled carbon nanotube (SWCNT) bundles with 2 keV electrons produces an increase in the Raman D peak. We find that an increase in the D peak does not occur when SWCNTs are preheated in situ at 600 C for 1 h in ultrahigh vacuum (UHV) before irradiation is performed. Exposing SWCNTs to air or other gases after preheating in UHV and before irradiation results in an increase in the D peak. Small diameter SWCNTs that are not preheated or preheated and exposed to air show a significant increase in the D and G bands after irradiation. X-ray photoelectron spectroscopy shows no chemical shifts in the C1s peak of SWCNTs that have been irradiated versus SWCNTs that have not been irradiated, suggesting that the increase in the D peak is not due to chemisorption of adsorbates on the nanotubes.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc955114 |
| Date | 12 1900 |
| Creators | Ecton, Philip |
| Contributors | Pérez, José M., Weathers, Duncan, Littler, Christopher, Srivilliputhur, Srinivasan, Verbeck, Guido |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Public, Ecton, Philip, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |
Page generated in 0.0026 seconds