Thin film coatings of (Cao.6Mg0.4)Zr4(P04)6 (CMZP) and Mg stabilized AhTiOs ( Mg-Ah Ti05 ) on dense SiC substrates were investigated using sol-gel coating techniques. The thickness and quality of both CMZP and Mg-Ah Ti05 coatings were found to depend on the solution concentration and lift rate. Double coatings were applied to obtain homogeneous and crack-free coatings. The quality of double coatings was influenced by different first and second coating thickness. The CMZP coated samples were fired in controlled atmospheres to have the pure CMZP phase. Unhydrolyzed solution of Mg-AhTiOs was utilized instead of hydrolyzed solution to improve the quality of Mg-AhTiOs coatings. Aging process was found to improve the quality of CMZP and Mg-Ah TiOs coatings. SiC samples coated with CMZP and Mg-Ah TiOs exhibited good thermal shock resistance and greatly improved the high temperature alkali corrosion resistance. / Master of Science
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/44351 |
| Date | 22 August 2008 |
| Creators | Yang, Shaokai |
| Contributors | Materials Science and Engineering, Brown, Jesse J. Jr., Hirschfeld, Deidre A., Kampe, Stephen L. |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Language | English |
| Detected Language | English |
| Type | Thesis, Text |
| Format | xiii, 103 leaves, BTD, application/pdf, application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | OCLC# 35217115, LD5655.V855_1996.Y364.pdf |
Page generated in 0.0012 seconds