A standard procedure for P3HT:PCBM bulk-heterojunction solar cells has been developed. Fabrication conditions, such as environment; solution concentration, thickness of active layer or post-treatment methods are systematically optimized. The best device performance is obtained by slow-drying spin-coated P3HT:PCBM (1:0.8) blend layer with DCB as solvent. C60:LiF composite films with up to 80% LiF concentration as hole blocking layer have been developed to significantly increase power conversion efficiencies of OPV devices. The short-circuit current density is greatly enhanced, without sacrificing open-circuit voltage and fill factor. Due to its superior oxygen diffusion blocking effect, the C60:LiF composite layer also can provide a more effective passivation film than a thin LiF layer, resulting in an impressive enhancement in air stability of devices.
Identifer | oai:union.ndltd.org:TORONTO/oai:tspace.library.utoronto.ca:1807/25593 |
Date | 31 December 2010 |
Creators | Gao, Dong |
Contributors | Lu, Zhenghong |
Source Sets | University of Toronto |
Language | en_ca |
Detected Language | English |
Type | Thesis |
Page generated in 0.0016 seconds