Low-temperature co-fired ceramic (LTCC) based system-in-package (SiP) is an emerging multilayer module technology for wireless communication applications, mainly due to its excellent high-frequency material properties. LTCC-SiP modules are typically soldered onto an organic motherboard, but the lifetime of the 2nd-level solder joints is often poor due to the high stress level of the joints in test/field conditions. Moreover, using lead-free solders in the interconnections of LTCC modules raised new questions about the feasibility and reliability of the solder joints in LTCC applications. Therefore, the characteristic features of the 2nd-level solder joint configuration were determined in this thesis work.
It was proved that collapsible Sn4Ag0.5Cu spheres are not a feasible option in LTCC/PWB assemblies with a large global thermal mismatch; a non-collapsible ball grid array (BGA) joint with a plastic core solder balls (PCSBs) was required to attain an adequate lifetime for such assemblies. To enhance the thermal fatigue endurance of the non-collapsible lead-free joints, a novel BGA joint consisting of Sn7In4.1Ag0.5Cu solder and PCSBs was developed. Moreover, this work proved that there is a relationship between the primary failure mechanisms of various Sn-based lead-free solders and thermomechanically induced stress level in the present non-collapsible BGA joint configuration.
The effect of the plating material of the solder lands on the failure mechanism of the BGA joints in the LTCC/PWB assemblies was studied. The results showed that the adverse phenomena related to the sintered Ag-based metallization materials can be avoided using electroless nickel with immersion gold (ENIG) as a deposit material. On the other hand, this study also demonstrated that the inadequate adhesion strength of the commercial base metallization in the ENIG-plated modules resulted in the disadvantageous failure mechanism of the test assemblies. Therefore, the criteria for material selection and the design aspects of reliable 2nd-level interconnections are discussed thoroughly in this thesis.
Identifer | oai:union.ndltd.org:oulo.fi/oai:oulu.fi:isbn978-951-42-6353-8 |
Date | 23 November 2010 |
Creators | Nousiainen, O. (Olli) |
Contributors | Karjalainen, P. (Pertti) |
Publisher | Oulun yliopisto |
Source Sets | University of Oulu |
Language | English |
Detected Language | English |
Type | info:eu-repo/semantics/doctoralThesis, info:eu-repo/semantics/publishedVersion |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess, © University of Oulu, 2010 |
Relation | info:eu-repo/semantics/altIdentifier/pissn/0355-3213, info:eu-repo/semantics/altIdentifier/eissn/1796-2226 |
Page generated in 0.0116 seconds