Previous issue date: 2014-09-01 / A lideran?a mundial brasileira na obten??o de etanol derivado da cana de a??car pode ser associada ? produ??o do vinhoto, em uma raz?o de 10 a 18 litros de vinhoto para cada litro de etanol produzido durante o processo de destila??o. Nos cultivos da cana-de-a??car, esse vinhoto tem sido aplicado como adubo org?nico, onde o seu bombeamento ? um elemento cr?tico dessa cadeia produtiva. O objetivo deste trabalho foi investigar os principais mecanismos de desgaste de um rotor e de partes de uma bomba centr?fuga ap?s bombear vinhoto tratado em reator (pH 7,3?0.5). Um filme de 300?75 ?m de metal duro ? base de carboneto de tungst?nio-cobalto (WC-Co) foi aplicado ao rotor de ferro fundido cinzento da bomba atrav?s da t?cnica de aspers?o t?rmica HVOF. Considerando-se os trinta anos de experi?ncia do autor no projeto de sistemas de bombeamento, uma bancada para o bombeamento de vinhoto a 27?2oC foi desenvolvida em Laborat?rio para um servi?o de 1.000 horas atrav?s de ensaios durante dez horas di?rias e cont?nuas de uma bomba modelo INI 32-125 operando sob condi??es de cavita??o, conforme o c?lculo de NPSH. Um sistema de recircula??o do vinhoto foi adotado e controlado por uma v?lvula de descarga empregada comumente em processos industriais. Ap?s os ensaios, tanto o rotor revestido pelo metal duro como algumas partes n?o revestidas da bomba apresentaram um desgaste severo por cavita??o-eros?o, enquanto partes do rotor onde os efeitos da cavita??o s?o menores, o revestimento apresentou um desgaste moderado. / The Brazilian capability concerning to the world's leading producer of sugarcane
ethanol can be joined together the vinasse production, which inherent
amount discharged by distilling is from 10 to18 liters of vinasse per liter of
ethanol produced. This vinasse has been applied in sugar-cane crops as
organic fertilizer, where its pumping process is a critical element in this string.
The aim of this work was investigate the main wear mechanisms of an impeller
and parts of a centrifugal pump after pumping vinasse treated in reactor (pH
8,3?0,7). A tungsten carbide-cobalt (WC10Co4%Cr) film based hard metal of
360?35?m ?m was applied on the grey cast iron pump impeller by HVOF
thermal aspersion. Based on the 30 years of experience of the author in the
design and mounting of pumping systems, a test rig was developed in
Laboratory for 1,000 hours of pumping tests of vinasse at 27?2oC for a
continuous service during 10 hours by day for a pump model 32-125, working
under cavitation conditions through the calculation of Net Positive Suction Head
(NPSH), A recirculating system of the vinasse was adopted and controlled by a
discharge valve usually employed in the industrial processes. After the tests,
both the coated rotor as the uncoated parts of the pump showed severe wear
by cavitation-erosion, while parts of the rotor where the effects of cavitation are
smaller, the coating showed a moderate wear.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/21681 |
| Date | 01 September 2014 |
| Creators | Augusto, Ant?nio Roberto |
| Contributors | 10973370491, Souza, Luiz Guilherme Meira de, 25094955420, Souza, Roberto Silva de, 44466927472, Medeiros, Jo?o Telesforo N?brega de |
| Publisher | PROGRAMA DE P?S-GRADUA??O EM ENGENHARIA MEC?NICA, UFRN, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0035 seconds