No / This study investigates the effect of heat treatment on changes in microstructure and wear behaviour of WC-NiCr coatings. Two feedstock powders with a similar chemical composition and different particle sizes (near nano-structured WC-17NiCr and microstructured WC-15NiCr) were used. High-velocity oxyfuel spraying technique was used to deposit coatings on to a mild steel substrate using identical spraying parameters. Coated samples were then heat treated in a nitrogen atmosphere at 500 and 700°C. The effect of heat treatment on changes in hardness and wear performance of the coatings was studied using microstructural analysis, micro-hardness indentation and abrasive wear tests. The results showed that the heat treatment increased the hardness of both coatings and a corresponding increase in wear resistance was recorded. The formation of a brittle CrWO4 phase in the microstructured coating resulted in brittle fracture of the coating and this gave lower wear resistance compared to the nanostructured coatings.
Identifer | oai:union.ndltd.org:BRADFORD/oai:bradscholars.brad.ac.uk:10454/17079 |
Date | 30 January 2017 |
Creators | Ben Mahmud, T., Khan, Tahir I., Farrokhzad, M.A. |
Source Sets | Bradford Scholars |
Language | English |
Detected Language | English |
Type | Article, No full-text in the repository |
Page generated in 0.0097 seconds