<p>U ovom radu prikazani su rezultati ispitivanja strukturnih i magnetnih osobina čistih cink- ferita, ZnFe<sub>2</sub>O<sub>4</sub> i cink-ferita sa dodatkom indijuma Zn<sub>1-x</sub>In<sub>x</sub>Fe<sub>2</sub>O<sub>4</sub> i itrijuma, ZnY<sub>x</sub>Fe<sub>2-x</sub>O<sub>4</sub>, gde je 0 ≤ x ≤ 0,6. Prahovi na bazi cink-ferita su sintetisani koristeći nisko temperaturnu metodu sinteze iz tečne faze – metodu koprecipitacije. Osnovni cilj ove doktorske disertacije je bio da se utvrdi veza između uslova sinteze, uticaja različitih katjona, strukture i osobina čistih cink-feritnih nanočestica, kao i cink-ferita sa dodatkom indijuma i itrijuma. Radi praćenja uticaja veličine čestica dobijenog praha na strukturu i osobine ovih materijala, sintetisani čist cink-ferit je kalcinisan na različitim temperaturama. Posebno je razmatran i uticaj dodatka različitih jona na distribuciju i preraspodelu katjona u spinelnoj strukturi. Pored toga ispitivan je uticaj tako pripremljenih prahova na njihove magnetne osobine. Rentgenostrukturna i TEM analize potvrdili su da ispitivani uzorci spadaju u klasu nanomaterijala spinelne strukture. Analiza Raman i Mössbauer spektara je ukazala na moguću raspodelu katjona između tetraedarskih i oktaedarskih mesta, te formiranje delimično inverznog spinela. Ispitivanja magnetnih osobina su pokazala da histerezisne petlje ne pokazuju saturaciju u prisustvu jakog magnetnog polja, što je potvrdilo superparamagnetnu i jednodomensku prirodu čestica. Pokazano je da pored uticaja veličine čestica, dodatak različitih katjona (u ovom slučaju itrijum i indijum) ima veliki uticaj na uređenje strukture, a posledično i na magnetno ponašanje ispitivanih nanočestičnih sistema.</p> / <p> This thesis presents the results of the investigation of the structural and magnetic properties of nanostructured zinc ferrites, ZnFe2O4 and zinc ferrites supstituted with different amount of indium and yttrium, Zn1-xInxFe2O4 and ZnYxFe2-xO4 (0 ≤ x ≤ 0,6). Powders based on zinc ferrites were synthesised by a low temperature wet-chemical method – coprecipitation. The main purpose of this thesis was to establish the relationship between the synthesis, dopants, structure and properties of zinc ferrite based materials. Nanoparticles of ZnFe2O4 were calcined at different temperatures in order to elucidate the influence of the particle size on the magnetic properties of the obtained nanoparticles. In addition, we have investigated the effect of dopant addition on cation distribution in spinel structure, in order to modify the magnetic properties and to obtain the magnetic ceramics with improved properties compared to the bulk-counterparts. The results of X-ray and TEM analyses confirmed the nanosized nature and spinel type structure of the investigated samples. Raman and Mössbauer spectroscopy studies implied on the possible cation distribution between the tetrahedral and octahedral sites and formation of the partially inversed spinel. The study of the magnetic properties showed that hysteresis loops do not saturate even in the presence of high magnetic fields, which confirmed the superparamagnetic and single domain nature of the samples. These observations imply that, besides the particle size, doping (e.g. yttrium and indium) causes significant structural rearrangements which in turn induce changes in magnetic behavior of the investigated nanoparticulate systems.</p>
Identifer | oai:union.ndltd.org:uns.ac.rs/oai:CRISUNS:(BISIS)82019 |
Date | 02 July 2010 |
Creators | Milanović Marija |
Contributors | Srdić Vladimir, Nikolić Ljubica, Rakić Srđan, Stojanović Goran |
Publisher | Univerzitet u Novom Sadu, Tehnološki fakultet Novi Sad, University of Novi Sad, Faculty of Technology at Novi Sad |
Source Sets | University of Novi Sad |
Language | Serbian |
Detected Language | Unknown |
Type | PhD thesis |
Format | application/pdf |
Page generated in 0.0014 seconds