The microstructure, and phase selections of La₆₆Al₁₄(Cu, Ni)₂₀ alloy were studied by Bridgman solidifications, and composite materials of dendrites in amorphous matrix or micro- and nano- sized eutectic matrix were formed with different cooling rates. The volume fraction of the dendrite phase reaches a maximum at the cooling rate of about 15 K/s, the secondary dendrite arm spacing λ₂ decreases from 4.3 µm to 0.6 µm with the increasing of cooling rate R, and obeys the equation of λ₂R⁰.⁵⁷=1.74µm(K/s)R⁰.⁵⁷. The compression strength, as well as the elastic strain limit of the dendrite/amorphous matrix composite are 600 MPa, and 2.3%, respectively. Improved ductility was observed for the dendrite amorphous matrix composites with more dendrite phase by slow cooling rate. / Singapore-MIT Alliance (SMA)
| Identifer | oai:union.ndltd.org:MIT/oai:dspace.mit.edu:1721.1/3824 |
| Date | 01 1900 |
| Creators | Zhang, Yong, Lee, Irene Mei Ling, Tan, Hao, Jing, Qin, Li, Yi |
| Source Sets | M.I.T. Theses and Dissertation |
| Language | en_US |
| Detected Language | English |
| Type | Article |
| Format | 619745 bytes, application/pdf |
| Relation | Advanced Materials for Micro- and Nano-Systems (AMMNS); |
Page generated in 0.0222 seconds