A Technique for Increasing the Optical Strength of Single-Crystal NaCl and KCl Through Temperature Cycling

This thesis relates a technique for increasing the optical strength of NaCl and KCl single-crystal samples. The 1.06-μm pulsed laser damage thresholds were increased by factors as large as 4.6 for a bulk NaCl single-crystal sample. The bulk laser damage breakdown threshold (LDBT) of the crystal was measured prior to and after heat treatment at 800*C using a Nd:YAG laser operating at 1.06 μm. Bulk and surface LDBTs were also studied on samples annealed at 400° C. These samples showed differences in damage morphology on both cleaved and polished surfaces, and the cleaved surfaces had improved damage thresholds. However, neither the polished surfaces nor the bulk showed improved threshold at the lower annealing temperature.

Identiferoai:union.ndltd.org:unt.edu/info:ark/67531/metadc504009
Date05 1900
CreatorsFranck, Jerome B. (Jerome Bruce)
ContributorsSoileau, M. J., Van Stryland, Eric W.
PublisherNorth Texas State University
Source SetsUniversity of North Texas
LanguageEnglish
Detected LanguageEnglish
TypeThesis or Dissertation
Formatv, 26 leaves : ill., Text
RightsPublic, Franck, Jerome B. (Jerome Bruce), Copyright, Copyright is held by the author, unless otherwise noted. All rights reserved.

Page generated in 0.0021 seconds