Avaliação de propriedades mecânicas e microestruturais de juntas de aços maraging soldadas por meio dos processos laser e feixe de elétrons / Evaluation of mechanical and microstructural properties of joints in maraging steel welded by laser and electron beam welding

Neste trabalho estudou-se as propriedades obtidas em juntas soldadas pelo processo de soldagem a laser do tipo estado sólido de onda contínua guiado por fibra, e os resultados foram comparados com juntas soldadas pelo processo feixe de elétrons. O material utilizado foi o aço maraging 350 - ASTM A 538 Grade C. As soldas realizadas com o processo feixe de elétrons possuem um procedimento de soldagem aprovado. A junta selecionada para a elaboração do trabalho foi do tipo sobreposta com material de base de espessuras diferentes, respectivamente iguais a 1,00 e 0,78 mm. As juntas soldadas foram avaliadas por: ensaio de cisalhamento, dureza Vickers e caracterização microestrutural das diversas regiões das juntas soldadas. Foram realizadas análises por microscopia óptica e microscopia eletrônica de varredura usando espectrometria de energia dispersiva (MEV/EDS). Foi realizado o teste de hipótese como técnica para a análise dos dados provenientes dos ensaios experimentais. Nas juntas soldadas com ambos processos não foi verificada a presença de descontinuidades, poros e depressões na superfície do cordão. Os resultados indicam que as condições usadas em ambos os processos de soldagem foram satisfatórias e possibilitaram a soldagem do aço maraging 350 atendendo aos requisitos necessários. / In this work, the welds made by a continuous wave diode pumped solid state laser guided by fiber were studied and the results were compared with welded joints of electron beam welding. The material used was maraging 350 steel ASTM A 538 Grade C. The welding process performed with electron beam welding has a approved welding procedure. The joint chosen for the preparation of the work was the lap joint type with different thicknesses base material respectively equal to 1,00 and 0,78 mm. The welded joints were evaluated by mechanical tests like shear test, Vickers hardness and microstructural characterization of the various regions of the welded joints. Analyzes were performed by optical microscopy and scanning electron microscopy using energy dispersive spectrometry (SEM/EDS). The hypothesis test technique was done for the analysis of data from experimental tests. For both welding process was not detected in the welded joints the presence of discontinuities, pores and depressions on the weld fillet surface. The results indicate that the conditions used for both welding process were satisfactory and allowed the welding of maraging 350 steel meeting necessary requirements.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-27052015-090049
Date07 May 2014
CreatorsMaximo, Henry Wilson Pohling
ContributorsNeves, Maurício David Martins das
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguageEnglish
TypeDissertação de Mestrado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0018 seconds