Svařování hlubokotažných ocelí s ochrannou vrstvou hybridní technologií Laser-TIG / Welding of deep-drawing steels with protective layer by laser-TIG hybrid technology

The diploma thesis focuses on laser welding of extra deep-drawn steel sheet according to the standard WSS-M1A365-A14 with a protective zinc surface layer. A 0,9 mm thick steel sheet with a zinc layer with coating weight 50 g · m^-2 is welded by a hybrid welding method Laser-TIG. The laser, as the primary energy source, is used for welding the material. The arc, provided by a non-melting tungsten electrode, is used for preheating the material for melting and evaporation of the zinc layer. Based on the initial experiments, the magnitude of the laser power with the welding speed was chosen as a constant parameter. The magnitude of the electric current, as the variable parameter, was set up to 0, 20, 30 and 40 ampers for welding the lap and the butt welds. Only one piece of the each weld type combination was made. The welds were afterwards tested to verify their quality and material properties. The first differences between laser welding with or without TIG preheating were visible during the experiment. The positive effects of the laser welding with preheating by TIG were confirmed. The material properties of the joints achieved better values and a influence of the welding defects on the quality of the joints was reduced. The Laser-TIG is a good choice for welding galvanized steel sheets in the mass production of automotive industry and it could be improved by more researches.

Identiferoai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:417119
Date January 2020
CreatorsBrehovský, Patrik
ContributorsSigmund, Marian, Mrňa, Libor
PublisherVysoké učení technické v Brně. Fakulta strojního inženýrství
Source SetsCzech ETDs
LanguageSlovak
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/masterThesis
Rightsinfo:eu-repo/semantics/restrictedAccess

Page generated in 0.0019 seconds