Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-11T12:08:27Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_InfluenciaParametrosTermicos.pdf: 3274679 bytes, checksum: 67a56351708ea6a0728c738561741289 (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-08-29T17:08:58Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_InfluenciaParametrosTermicos.pdf: 3274679 bytes, checksum: 67a56351708ea6a0728c738561741289 (MD5) / Made available in DSpace on 2014-08-29T17:08:58Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_InfluenciaParametrosTermicos.pdf: 3274679 bytes, checksum: 67a56351708ea6a0728c738561741289 (MD5)
Previous issue date: 2007 / CEFET/PA - Centro Federal de Educação Tecnológica do Pará / O principal objetivo deste trabalho é desenvolver um estudo teórico/experimental sobre a influência dos parâmetros térmicos de solidificação (V L e T) na transição colunar/equiaxial das ligas Sn 5%Pb, Sn 15%Pb, Sn 20%Pb e Sn 25%Pb sob condições de solidificação unidirecional horizontal refrigerada à água. Inicialmente, são calculadas experimentalmente as velocidades da isoterma líquidus e as taxas de resfriamento das ligas em questão cujos resultados são comparados com as previsões teóricas de um modelo numérico. Em seguida, a posição da transição colunar/equiaxial é determinada por meio da análise macroestrutural assim como são avaliados os efeitos impostos por correntes convectivas devido ao efeito do
soluto no comportamento da transição colunar/equiaxial das referidas ligas. Finalmente, é
realizado um estudo experimental comparativo para as ligas estudadas quando solidificadas
unidirecionalmente em diferentes sistemas refrigerados à água. / This work carry out a theoretical experimental study about the influence of solidification
thermal parameters on the columnar to equiaxed transition of Sn 5%Pb, Sn 15%Pb, and Sn
20% Pb and Sn 25% Pb alloys during the horizontal unidirectional solidification process
cooled by water which considers the solute convection effects. The tip growth rates and
cooling rates have been experimentally calculated and the obtained results are compared with
those of a numerical model. The columnar to equiaxed transition position is determined
through the macrostructure characterization of the studied alloys. The experimental results
have shown that the thermosolutal convection influences the CET occurrence. Finally, a
comparative experimental study is done for the studied alloys when directionally solidified in
different water-cooled systems.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/5559 |
Date | 04 July 2007 |
Creators | MOUTINHO, Daniel Joaquim da Conceição |
Contributors | MOREIRA, Antonio Luciano Seabra, ROCHA, Otávio Fernandes Lima da |
Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia Mecânica, UFPA, Brasil, Instituto de Tecnologia |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds