Análise microestrutural, tenacidade à fratura e vida em fadiga das AA7050-T7451 e AA2050-T84 (Al-Li) / Microstructural analysis, fracture toughness and fatigue life of AA7050-T7451 and AA2050-T84 (Al-Li) alloys

No presente trabalho foi realizado um estudo comparativo entre as ligas AA7050- T7451 e AA2050-T84, bem como entre as direções L-T e T-L para analisar o comportamento das ligas, quando submetidos à temperatura ambiente e criogênica. Para realizar a análise comparativa entre as ligas e entre as direções, foram utilizados corpos de prova tipo C(T) (Compacto Tension), pré-trincados em fadiga. A análise comportamental das ligas foram avaliadas através dos ensaios de tenacidade à fratura, KIC, Curva KR, fadiga, da/dN. A microestrutura foi caracterizada através da microscopia ótica, microscopia eletrônica de varredura e microscopia eletrônica de transmissão. Foi observado que na direção L-T há uma maior resistência à propagação da trinca em relação à direção T-L, no que diz respeito à Curva KR, tanto para temperatura ambiente quanto para temperatura criogênica. Quando comparou-se as duas ligas na direção L-T em temperatura ambiente, ambas apresentaram um fator de intensidade de tensão similar. Os resultados dos ensaios de fadiga mostraram que a direção T-L é mais sensível à razão de carga. Analisando os resultados entre as direções L-T e T-L, observou-se que as duas ligas apresentaram comportamento anisotrópico. / A comparative study was made of the AA7050-T7451 and AA2050-T84 alloys and of the L-T and T-L directions to analyze the behavior of the alloys when subjected to room and cryogenic temperatures. The comparative analyses of the alloys and directions were performed using fatigue-precracked compact tension (CT) test specimens. The behavior of the alloys was analyzed based on fracture toughness, KIC, KR curve, fatigue, and da/dN tests. Their microstructure was characterized by optical microscopy, scanning electron microscopy and transmission electron microscopy. The KR curve indicated that resistance to crack propagation was higher in the L-T direction than in the T-L direction at both room and cryogenic temperatures. In a comparison of the two alloys in the L-T direction at room temperature, they were found to present a similar stress intensity factor. The results of the fatigue tests demonstrated that the T-L direction is more sensitive to the load ratio. An analysis of the results in the L-T and T-L directions indicated that the two alloys exhibited anisotropic behavior.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-24072015-173030
Date23 February 2015
CreatorsPascoal Júnior, Fernando Antonio
ContributorsBose Filho, Waldek Wladimir
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguagePortuguese
TypeTese de Doutorado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0025 seconds