000755310.pdf: 4444260 bytes, checksum: da0afdb8588e7917a1f1fd0fc00f6b92 (MD5) / O aumento das exigências mundiais por melhores produtos e a crescente competição entre empresas no mercado globalizado aumenta a busca por processos que garantam menores custos aliados a grande produtividade e produto de alta qualidade. Assim o grande desenvolvimento industrial e tecnológico tem aumentado a pesquisa em processos de usinagem que promovam, por exemplo, alto desempenho no que diz respeito à remoção de material, menor avaria e desgaste da ferramenta e menores impactos ao meio ambiente. Em relação às superligas a base de níquel, as mesmas têm um papel extremamente importante nas indústrias aeronáutica, automobilística, petróleo e gás dentre outras. As superligas a base de níquel estudadas foram a Nimonic 80A, o Inconel 718 e a Pyromet A31, materiais de difícil usinagem que possuem alta resistência mecânica e à corrosão em temperaturas elevadas. O objetivo deste trabalho é o estudo da formação do cavaco em relação aos diversos parâmetros de usinagem, a fim de alcançar alto desempenho e melhorias no torneamento cilíndrico externo destas ligas. As ligas foram torneadas utilizando-se diversos parâmetros de usinagem: velocidades de corte (75 e 90 m/min), avanço (0,15 e 0,18 mm/rot), profundidade (0,8 mm), Mínima Quantidade de Fluido (MQF), Fluido abundante e ferramenta de metal duro com recobrimento (TiAlN). Analisou-se a formação de cavacos, a rugosidade do material, o volume de material removido, o comprimento usinado. Foram realizadas ainda análises macroestruturais e de tempo de vida das ferramentas utilizadas a fim de se detectar possíveis desgastes, bem como análises microestruturais dos cavacos através da microscopia óptica e das ferramentas por microscopia eletrônica de varredura (MEV) e espectroscopia de energia dispersiva (EDS). Assim foi possível notar que há mais de um tipo de desgaste associado... / The increase of world requirements per better products and the growing competition between companies in the global market makes them seek processes that ensure lower costs allied to high productivity and high quality product. Thus the great industrial and technological development has increased the search for machining processes that promote, for example, high performance as regards the chip removal, less tool wear and failure and reduced impact on the environment. Regarding superalloys based on nickel, they have an extremely important role in the aeronautical and automotive industries among others. The nickel-based superalloy studied are the Nimonic 80A, Inconel 718, Pyromet A31 difficult to machine materials that has high mechanical strength and corrosion resistance at higher temperatures. The objective of this work is to study the influence of the application of cutting fluids in turning and the machining parameters in order to achieve high performance and optimization of machining this alloys. The alloys were machined using various machining parameters: cutting speed (75 and 90 m/min), feed rate (0,15 and 0,18 mm/rot), cutting depth (0,8 mm), Minimum Quantity fluid (MQF), Fluid abundant and coated tools. After turning chip samples were obtained, was measured the surface roughness, chip volume removed, cutting length and macrostructural analyzes were performed and of lifetime of the tools used in order to detect possible wear, as well as, microstructural analyzes of the chips by optical microscopy and tools by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Thus it was possible to note that there is more than one type of wear associated the turning of nickel alloys, as well as the cutting speed of 75 m/min was the best in general terms for use of abundant fluid. Regarding the application of MQF obtained satisfactory ... (Complete abstract click electronic access below)
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/94380 |
| Date | 11 February 2014 |
| Creators | Gama, Renann Pereira [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Ribeiro, Marcos Valério [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 128 f. il. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.004 seconds