Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T09:04:33Z (GMT). No. of bitstreams: 1
Alves_ElianeBemerguy_D.pdf: 642464 bytes, checksum: a986353a680e6d427281d2a4f0c5d3e7 (MD5)
Previous issue date: 2005 / Resumo: O objetivo deste estudo foi avaliar a adaptação marginal e a dureza Knoop da resina Filtek Z250, cor A2 (3M-ESPE) utilizada para restaurar 90 cavidades, com margens em dentina, confeccionadas na face vestibular de incisivos bovinos, empregando três técnicas e três métodos de fotoativação. As cavidades foram padronizadas com dimensões de 3mm no sentido mesio-distal; 3mm no sentido inciso-cervical e 1,5mm de profundidade. Os grupos, com 10 restaurações cada, foram divididos de acordo com a técnica de fotoativação: direta; transdental ou mista, e método de fotoativação, que correspondem a variações na fonte de luz: halógena com 600mW/cm² (XL 2500/3M), arco de plasma de xenônio com 1340mW/cm² (Apollo 95E/DMD) e LED com 500mW/cm² (Ultrablue IS/DMC). Os tempos para cada etapa de fotoativação foram estabelecidos em 20s para os aparelhos fotoativadores Ultrablue IS e XL 2500 e 9s para o Apollo 95E. A análise da adaptação marginal foi realizada em fotos digitais, obtidas das superfícies das restaurações, após 24 horas de armazenagem, polimento padronizado e pigmentação com vermelho ácido a 1% em propileno glicol (Caries Detector- Kuraray). Foi utilizado o programa analisador de imagens, UTHSCSA - Image Tool, tendo como referência a medida de 1mm de um paquímetro digital (Mitutoyo, Japão) escaneado junto com cada restauração. As medidas de dureza Knoop foram obtidas no topo e na base da restauração, usando o microdurômetro HMV 2 (Shimadzu-Japão) com carga de 50 gramas atuando por 15 segundos. Em cada corpo-de-prova foram feitas seis endentações. Os dados foram submetidos à Análise de Variância e as médias comparadas pelo teste de Tukey (5%) e mostraram que independente do tipo de unidade fotoativadora, o emprego da técnica mista reduziu o percentual de fendas entre o material restaurador e o dente, determinando melhor adaptação marginal em relação à técnica direta, sendo que a técnica transdental não diferiu estatisticamente das demais. A adaptação marginal não foi influenciada pelas diferentes unidades de fotoativação utilizadas neste estudo, quando comparadas dentro da mesma técnica. A técnica de fotoativação direta apresentou as maiores médias de dureza em relação à mista e transdental, sendo que a transdental apresentou os menores valores de dureza. Independente da técnica de fotoativação empregada, o aparelho LED (Ultrablue IS) apresentou os maiores valores de dureza em relação ao Apollo 95E. Nenhuma diferença estatística foi observada nos valores de dureza Knoop entre os aparelhos LED e XL 2500 e XL 2500 e Apollo 95E / Abstract: The aim of this study was to evaluate marginal adaptation and Knoop hardness of the resin Filtek Z250 A2 (3M-ESPE). Ninety cavities, with margins in dentine, in the vestibular face of incisive bovine teeth were restored using three techniques and three photoactivation methods. The cavities were standardized with dimensions: 3mm mesio-distal; 3mm incisive-cervical, and 1.5mm deep. The groups, with 10 restorations each, were divided according to the photoactivation technique: direct; transdental or mixed, and method of photoactivation that correspond to variations in the light source: halogen light with 600mW/cm² (XL 2500/3M), xenon plasma arc with 1340 mW/cm² (Apollo 95E/DMD) and LED with 500mW/cm² (Ultrablue IS/DMC). The periods for each photoactivation stage were established in 20s for the units Ultrablue IS and XL 2500 and 9 s for the Apollo 95E. Marginal adaptation analysis was carried out in digital photografy, obtained from the surfaces of restorations, 24 hours after storage, with standard polish and with red acid pigmentation at 1% in propylene glycol (Cáries Detector - Kuraray). The program image analyzer, UTHSCSA - Image Tool was used , having as reference the measure of 1mm of a digital caliper (Mitutoyo, Japan) scanned with each restoration. The measures of Knoop hardness were obtained on the top and on the base of the restoration, using the microhardness unit HMV 2 (Shimadzu-Japan) with load of 50 grams for 15 seconds. In each specimen were made six indentations. The data were submitted to the Analysis of Variance and the averages compared by Tukey's test (5%) and showed that independent of the type of photoactivating unit the use of the mixed technique reduced the percentile of gaps between the restoring material and the tooth, determining better marginal adaptation in relation to the direct technique. The transdental technique did not differ statistically from the others. The marginal adaptation was not influenced by the different photoactivation units used in this study, when compared inside the same technique. The technique of direct photoactivation showed the highest averages of hardness in relation to the mixed and transdental ones, and the transdental presented the lowest hardness values. Independent of the photoactivation technique used, the Ultrablue IS nit presented the highest hardness values in relation to Apollo 95E. No statistical difference was observed on hardness values between the units Ultrablue IS and XL 2500 and XL 2500 and Apollo 95E / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289587 |
| Date | 14 September 2005 |
| Creators | Alves, Eliane Bemerguy |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Correr Sobrinho, Lourenço, 1960-, Konno, Alysson Noriyuki Kajishima, Chavez, Oscar Fernando Muñoz, Sinhoreti, Mário Alexandre Coelho, Rontani, Regina Maria Puppin |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 116p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds