Thesis summarizes the problems of production and use of stretch film. The change of strength, ductility and relative relaxation effect in different times of drawing from role in three weeks was observed. Further, change of strength and ductility due to changes in the rate of deformation, exposure to accelerated aging in a UV chamber and changes in the loading direction were observed. Mechanical tests were realized on a tensile tester, relaxation tests on DMA and crystallinity changes were observed on the DSC. Relationship between chemical composition of stretch film and mechanical and thermomechanical properties were studied. It was found that chemical composition essential for stretch film properties. However, due to the impossibility to distinguish effects of chemical composition and process parameters was impossible to find clear relation describing this relationship.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:217140 |
| Date | January 2015 |
| Creators | Vojáček, Jakub |
| Contributors | Tocháček, Jiří, Poláček, Petr |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0024 seconds