Previous issue date: 2014-08-29 / O interesse pela utilização de resíduos industriais, tais como lodo tem crescido como alternativa tanto na redução do volume desse passivo ambiental quanto na obtenção de um produto a ser utilizado na construção civil. Este trabalho tem como objetivo desenvolver e avaliar as propriedades físico-mecânicas de concretos formados a partir do uso de lodo da indústria têxtil, visando sua aplicação na construção civil. O lodo têxtil foi seco em estufa a 110ºC por vinte e quatro horas e triturado em moinho para adquirir granulometria adequada e em seguida submetido às seguintes análises: termogravimetria, análise térmica diferencial, espectroscopia vibracional de absorção no infravermelho, difração de raios-X, análise química, lixiviação, solubilização e microscopia óptica. Foram confeccionados corpos de prova de concreto utilizando os traços 1:3 e 1:4 com teores de substituição de 0 %, 3 %, 5 % e 7 % de lodo no agregado miúdo, com 7, 28 e 60 dias de cura e realizaram-se os seguintes ensaios: abatimento do tronco do cone, de resistência à compressão axial, resistência à compressão diametral, absorção, índice de vazios, massa especifica, microscopia óptica, microscopia eletrônica de varredura, lixiviação e solubilização. Os resultados das caracterizações do lodo têxtil apresentaram a compatibilidade química e estabilidade térmica suficiente para sua incorporação no concreto, entretanto verificou um alto teor de matéria orgânica. Já o ensaio de lixiviação classificou o lodo têxtil como resíduo perigoso, devido o extrato lixiviado ultrapassar o limite para os metais ferro e manganês. Já nos corpos de provas os ensaios de lixiviação e solubilização mostraram que os metais encontram-se encapsulados no concreto com teores de até 7 % de lodo têxtil. Nas microscopias realizadas nos corpos de provas de concretos, verificou-se a pouca interação do lodo com os constituintes do concreto. Já a absorção de água apresentou uma tendência de aumento, quando cresceu a quantidade de lodo têxtil, mas os valores ficaram abaixo de 10 %, podendo ser considerado de boa qualidade. No que se refere aos resultados de resistência à compressão ocorreu uma diminuição desta com o teor de lodo têxtil. No traço 1:3 com teores de até 7 % de lodo e no traço 1:4 com até 5 % de lodo o concreto foi considerado moderado, e para o traço 1:4 com 7 % de lodo foi classificado como concreto não estrutural. / Interesting in the use of industrial waste, such as sludge has grown both as an alternative in reducing the volume of this environmental liability as in getting a product to be used in civil building. This work aims to develop and evaluate physical and mechanical properties of concrete formed from the use of textile industry sludge, for its application in civil building. The textile sludge was dried at 110°C for twenty-four hours and milled in a grinder to get proper particle size and then subjected to the following tests: thermogravimetry, differential thermal analysis, vibrational infrared absorption spectroscopy, X-ray diffraction,chemical analysis, leaching, solubilization and optical microscopy. Concrete specimens were fabricated using the ratios 1:3 and 1:4 under levels of sludge substitution of 0 %, 3 %, 5 % and 7 % in the small aggregate, with7, 28 and 60 days of curing and performed the following tests: cone trunk reduction, compressive strength, tensile splitting strength, absorption, void ratio, specific gravity, optical microscopy, scanning electron microscopy, and leaching. The results of the textile sludgecharacterizations showed the chemical compatibility and thermal stability sufficient for its incorporation in concrete, however it was found a high content of organic matter. Again, leaching test rated the textile sludge dangerousand, because the extract leaching exceed the limit for the metals iron and manganese. The sample tests regarding solubilizatio and leaching tests showed that metals are encapsulated in concrete with levels of up to 7 % of textile sludge. In microscopy performed on test samples of concrete, there was a little interaction with the sludge constituents of the concrete. The water absorption presented increase trend when increased the amount of textile sludge, but the values were below 10 % and can be considered good quality. Regarding theresults of compressive strength occurred decrease relatedto the textile sludge content. On the ratio 1:3, with sludge levels up to 7 %, and the ratio 1: 4 up to 5 % of suldge level, the the concrete was considered moderate, and the ratio 1:4 up to 7 % of sludge, the concrete was classified as non structural.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/251 |
Date | 02 February 2018 |
Creators | ALTIDIS, Marina Elizabeth Dias. |
Contributors | MORAIS, Crislene Rodrigues da Silva., BRITO, André Luiz Fiquene de., NASCIMENTO, José Wallace Barbosa do., CAVALCANTI, Maria do Socorro Lopes., ALEXANDRE, Jonas. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0015 seconds