Avaliação da ação da florescência em cerâmica vermelha com adição de lodo de fosfatização

Submitted by Nara Lays Domingues Viana Oliveira (naradv) on 2015-08-05T19:25:05Z
No. of bitstreams: 1
RosangelaBerschEngCivil.pdf: 4573683 bytes, checksum: bcd59ec2871283c130461a507acc1ace (MD5) / Made available in DSpace on 2015-08-05T19:25:05Z (GMT). No. of bitstreams: 1
RosangelaBerschEngCivil.pdf: 4573683 bytes, checksum: bcd59ec2871283c130461a507acc1ace (MD5)
Previous issue date: 2011-03-03 / PROSUP - Programa de Suporte à Pós-Gradução de Instituições de Ensino Particulares / A cristalização de sais é uma patologia importante e freqüentemente observada em alvenarias. No entanto é ainda uma das patologias menos compreendidas. O objetivo deste trabalho é justamente avaliar o impacto da florescência de sais solúveis em corpos-de-prova cerâmicos desenvolvidos com lodo de fosfatização. Para tanto, foram moldados corpos-de-prova com 0; 2,5% e 5% (em peso) de lodo, os quais foram sinterizados a temperatura de 750ºC, 850ºC, 950ºC e 1050ºC. Os corpos-de-prova foram divididos em dois grupos, dos quais um foi mantido sob temperatura e umidade controladas e o outro, submetido a ciclos de molhagem e secagem. Os grupos foram ensaiados em 1, 30, 110 e 180 dias. Foram submetidos à análise de imagem (através de Lupa binocular, software gráfico e microscopia eletrônica de varredura), absorção de água por capilaridade, porosimetria por intrusão de mercúrio e resistência à flexão. Para análise química e das fases presentes, foram realizadas análises via difração de raios-x, fluorescência de raios-x e espectrometria de emissão atômica. Os resultados indicam a presença de alumínio, silício, cálcio, potássio, enxofre, ferro e manganês, dos quais se destaca a combinação entre o enxofre e cálcio. Desta forma, a gipsita é tida como provável responsável pelos sais solúveis, cujos depósitos foram encontrados sob variada extensão e intensidade, predominado nos corposde-prova com adição de lodo. A variação da porosidade e a aparente diminuição do coeficiente de absorção capilar ao longo dos ensaios podem ser associadas aos processos de solubilização e recristalização da gipsita. No tempo de ciclagem estudado, o fenômeno não apresentou influência na resistência mecânica dos corpos-de-prova. / The crystallization of salts is an important and frequently observed pathology in masonry. However, it is still one of the least understood pathologies. The aim of this study is to evaluate the impact of florescence of soluble salts in ceramic blocks developed with phosphate sludge. For this purpose, blocks were molded with 0, 2.5% and 5% of phosphate sludge, which were sintered at temperatures of 750°C, 850°C, 950°C and 1050 ° C. The blocks were divided into two groups, one of which was kept under controlled temperature and humidity and the other was subjected to wetting and drying cycles. The groups were tested at 1, 30, 110 and 180 days. They were subjected to image analysis (binocular magnifying glass, graphic software and scanning electron microscopy), capillary water absorption, mercury intrusion porosimetry and flexural strength. The methods, x-ray diffraction, x-ray fluorescence and emission spectrometry, were used to investigate the phase and chemical composition. The results indicate the presence of aluminum, silicon, calcium, potassium, sulfur, iron and manganese, among which stands out the combination of sulfur and calcium. Thus, the gypsite is considered to be likely responsible for the soluble salts, whose deposits were found in varying extent and intensity, prevailing in the blocks with addition of waste. The variation in porosity and the apparent decrease in the coefficient of capillary absorption along the tests may be associated with the processes of solubilization and recrystallization. In cycling time studied, the phenomenon did not influence the mechanical strength of specimens.

Identiferoai:union.ndltd.org:IBICT/oai:www.repositorio.jesuita.org.br:UNISINOS/4683
Date03 March 2011
CreatorsBersch, Rosângela Andréia
Contributorshttp://lattes.cnpq.br/8126174297312115, Brehm, Feliciane Andrade
PublisherUniversidade do Vale do Rio dos Sinos, Programa de Pós-Graduação em Engenharia Civil, Unisinos, Brasil, Escola Politécnica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UNISINOS, instname:Universidade do Vale do Rio dos Sinos, instacron:UNISINOS
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0028 seconds