The effect of initial microstructures of an 0.05 wt.% C low carbon steel, acicular ferrite (AF), Bainite (B), polygonal ferrite (PF), fine polygonal ferrite (FPF), and a microstructure produced by direct strip casting (DSC) (termed SC), on the deformation and recrystallization behaviour of cold rolled low carbon (LC) steel, was investigated. The initially prepared samples with the initial microstructures were cold rolled to 50, 70 and 90% reductions, then annealed isothermally in the temperature range 580 ??? 680 oC. The microstructures and textures produced by deformation and annealing were studied by optical microscopy, XRD, TEM, SEM and EBSD. The initial microstructures were characterized mainly by optical microscopy and EBSD. Using EBSD, the ferrite grain size of the AF, B and SC samples was considerably larger than that found by optical microscopy with a large fraction of low angle grain boundaries (LAGBs) observed within prior austenite grains. All samples exhibited a very weak texture close to random. After cold rolling, the microstructures of AF and SC contained shear bands with PF and FPF generating deformation bands. For AF and SC, the pearlite phase was more extensively elongated in rolling direction compared with PF and FPF. After 90% cold rolling reduction, PF, FPF and SC consist mainly of the texture component and AF and B . It was found that FPF recrystallized most rapidly followed by B, PF and AF with SC recrystallizing orders of magnitude more slowly due to the solution drag caused by its uniformly distributed higher Mn content. Very strong (???-fibre) texture was generated in cold rolled PF followed by FPF, with AF, SC and B generating very weak textures. The texture evolution during annealing 90% reduction PF was examined in further detail. The behaviour of nucleation and grain growth provides strong evidence of orientated nucleation as the dominant factor for CRA texture development in this material.
| Identifer | oai:union.ndltd.org:ADTP/257213 |
| Date | January 2006 |
| Creators | Xu, Wanqiang, Materials Science & Engineering, Faculty of Science, UNSW |
| Publisher | Awarded by:University of New South Wales. School of Materials Science and Engineering |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | Copyright Wanqiang Xu, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0012 seconds