Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2014. / Made available in DSpace on 2015-02-05T21:06:55Z (GMT). No. of bitstreams: 1
328376.pdf: 5992091 bytes, checksum: a10fa03b115205f889f0efd5ddcf76a8 (MD5)
Previous issue date: 2014 / O objetivo principal deste trabalho é desenvolver películas finas de polidimetilsiloxano (PDMS) capazes de extrair luz de lâmpadas de diodo orgânico emissor de luz (OLED), provocando um aumento na eficácia luminosa. Diversos materiais e superfícies foram utilizados como molde para o desenvolvimento dos filmes de PDMS cujas superfícies foram caracterizadas utilizando-se perfilometria, interferometria óptica e microscopia eletrônica por varredura. Após a caracterização estrutural, os filmes de PDMS foram aplicados sobre o vidro da lâmpada OLED e a sua influência sobre a eficácia luminosa foi avaliada por meio da caracterização elétrica em esfera integradora. Na caracterização elétrica avaliou-se que os filmes obtidos utilizando-se vidro litografado proporcionaram aumentos na eficácia luminosa de 11% (filme com discos de 80 µm de diâmetro), de 16% (filme com discos de 20 µm de diâmetro) e de 22% (filme com discos de 50 µm de diâmetro). Um filme desenvolvido utilizando-se lixa comercial de granulometria de 1200 proporcionou um aumento da eficácia luminosa de 26%. O melhor resultado obtido no aumento da eficácia luminosa foi de 36% com a utilização do filme PDMS obtido a partir da utilização de vidro comercial jateado como molde, cujo resultado é similar ao obtido utilizando-se filme comercial. Em análise por meio de perfilometria, interferometria e microscopia eletrônica, evidenciou-se que os resultados mais expressivos no aumento da eficácia luminosa foram aqueles cuja rugosidade média quadrática do filme de PDMS era em torno de 5 µm e cujos picos possuem altura média em torno de 20 µm.<br> / Abstract : The main objective of this work is to develop polydimethylsiloxane (PDMS) thin film capable of extracting light from organic light emitting diode (OLED) lamps, increasing its luminous efficacy. Various materials and surfaces were used as substrate for the development of PDMS films whose surfaces were characterized using profilometry, interferometry and scanning electron microscopy. After the structural characterization, the PDMS films were applied on the OLED lamp glass and its influence on the luminous efficacy was assessed by electrical characterization in an integrating sphere. In the electrical characterization the films using lithographed glass increased the luminous efficacy by 11 % (film with discs with diameters of 80 µm), 16% (film with discs with diameters of 20 µm) and 22 % (film with discs with diameters of 50 µm). A film developed using commercial particle size of 1200 grit sandpaper increased the luminous efficacy in 26%. The best result in enhancing the luminous efficiency was 36% using the film obtained from the use of commercial sandblasted glass as substrate, which is similar to that obtained using commercial film. The analysis by profilometry, interferometry and electron microscopy showed that the most dramatic results in increasing the luminous efficacy were those whose mean square roughness of the PDMS film was around 5 µm and whose peaks have average height around 20 µm.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/129454 |
| Date | January 2014 |
| Creators | Vicente, Cristiano |
| Contributors | Universidade Federal de Santa Catarina, Pasa, André Avelino, Zoldan, Vinicius Claudio |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | xxiv, 65 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds