The aim of this diploma thesis is to investigate microstructure and thermal stability of ultra fine grained magnesium alloys. The thesis first summarises methods using plastic deformation in order to achieve ultra fine grained structure that are used to process metals. Then experimental methods employed in the experimental part including microhardness testing, scanning electron microscopy and positron annihilation spectroscopy are described. Brief summary of previous research on MgZnY alloys strengthened by quasicrystalline phases and Mg22Gd alloys is given. Finally, results of experimental investigation of MgZnY alloys with various Zn/Y ratios and Mg22Gd alloy are discussed. These results suggest that presence of phases in MgZnY alloys depend on Zn/Y ratio, hardness of these alloys depends on Zn content and that rapid cooling of MgZnY alloys annealed at 500 řC lead to significant increase in volume fraction of quasicrystalline icosahedral phase. In the second section of the experimental part thermal behaviour of Mg22Gd alloy is investigated. Furthermore, formation of GdH2 particles in Mg22Gd is examined and attributed to reaction of hydrogen decomposed from water vapour with gadolinium in areas rich in gadolinium. Finally, significant hardening of Mg22Gd alloy processed by high pressure torsion has been...
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:368163 |
Date | January 2017 |
Creators | Vlasák, Tomáš |
Contributors | Čížek, Jakub, Procházka, Ivan |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0015 seconds