The aim of this master’s thesis is electrochemical characteristics evaluation of magnesium alloys. The theoretical part describes the properties of magnesium and its alloys and their corrosion characteristics. In the experimental part are presented results of corrosion resistance measurement of two types of wrought magnesium alloys. It was AZ31 and AZ61 magnesium alloys, which were measured in Hank’s solutions with addition of ions Ca2+ and Mg2+ (SBF+) and without addition of the ions (SBF). The solution temperature during the measurement was 37 ± 1 °C. The experiments were used electrochemical impedance spectroscopy (EIS) and potentiodynamic tests using linear polarization (LP). EIS measurements were done in times of 5 minutes, 1, 2, 4, 8, 12, 24, 48, 72, 96 and 168 hours. Potentiodynamic tests were only short-term and they started after 5 minutes of stabilization. Both methods were used for measuring the electrochemical characteristics of polished and ground surface of the samples. The most important measurement results were polarization resistance, corrosion potential and corrosion current density. The electrochemical measurements are used to estimate the chemical composition influence and alloy’s structure of the corrosion resistance.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:240550 |
| Date | January 2016 |
| Creators | Slouková, Karolína |
| Contributors | Hadzima, Branislav, Tkacz, Jakub |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0015 seconds