It’s well known that MnAl(C) material consists of a metastable phase (τ) with promising ferromagnetic properties, produced either by controlled cooling from the high-temperature hexagonal ε-phase or rapid cooling that freezes the ε-phase followed by low-temperature annealing. Due to the high cooling rates involved, additive manufacturing (AM) especially selective laser melting (SLM), has been identified as a possible method to retain the high-temperature ε-phase, hence containing a potential capacity to produce permanent magnets upon low-temperature annealing. Moreover, the competency of additive manufacturing to address manufacturing design complexity, material scarcity and tailored properties, yields a great opportunity to produce permanent magnets with suitable magnetic properties for complex applications. This work provides a systematic study on three main aspects; development of printing parameters for improved relative density of as-printed MnAl(C) samples; investigation of the influence of scanning strategies on the crystallographic texture of as-printed and annealed samples; investigation of the influence of annealing time and temperature on τ-phase purity and magnetic properties. It was found that laser remelting (multiple laser exposure) combined with specific scanning strategies is a promising path to enhance the relative density of as-printed samples. Some specific scanning strategies were found to be capable of retaining relatively strong crystallographic textured ε-phase in as-printed samples. Following the annealing process for ε→τ transformation, only a partial transformation of crystallographic texture was observed. Characterization of annealed samples through XRD (x-ray diffraction) and phase fractions calculations through Rietveld refinement reveals that relatively short annealing times and low temperatures result in incomplete ε→τ transformation. In addition, longer annealing times and higher temperatures surpass the complete ε→τ transformation and lead to the formation of equilibrium phases subsequently reducing the magnetic performance. Furthermore, the experimental findings demonstrated a pronounced influence of higher carbon content in the powder, resulting in improved magnetic properties.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-507653 |
Date | January 2023 |
Creators | Abenayake, Himesha |
Publisher | Uppsala universitet, Tillämpad materialvetenskap, Uppsala universitet, Oorganisk kemi |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | MATVET Additiv ; 23003 |
Page generated in 0.0016 seconds