Ensaios uniaxiais e biaxiais para avalição de criterio de resistencia de materiais anisotropicos aplicado a madeira / Uniaxial and biaxial tests for avaliation of failure criterion of anisotropic material applied to wood

Orientador: Nilson Tadeu Mascia / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil, Arquitetura e Urbanismo / Made available in DSpace on 2018-08-12T16:59:12Z (GMT). No. of bitstreams: 1
Todeschini_Rodrigo_M.pdf: 5391907 bytes, checksum: 209282e318155e52af17d68ae99c2ffb (MD5)
Previous issue date: 2009 / Resumo: A realização de ensaios uniaxiais e biaxiais permite uma melhor compreensão do comportamento mecânico de um material que possui direções principais de resistência e é sem dúvida uma forma que pesquisadores encontraram para obter resultados condizentes com a situação real que uma determinada estrutura apresenta. O presente trabalho teve como objetivo o estudo do critério de resistência proposto por Tsai e Wu, realizando-se ensaios uniaxiais e biaxiais. A avaliação do critério ficou restrita ao ensaio de compressão, devido às dificuldades de se realizar ensaios biaxiais de tração. Com o ensaio biaxial de compressão, tensões em duas direções principais foram simultaneamente desenvolvidas, utilizando-se um equipamento de ensaio tradicional para uma direção e na direção perpendicular um equipamento tipo alicate desenvolvido para este fim. O parâmetro estudado foi o 12 F , parâmetro este que designa a possibilidade da superfície de ruptura ser aberta ou fechada, considerando-se que para a segurança de um projeto é imprescindível obter uma superfície fechada para o critério de resistência adotado. Observa-se, além disso, que o parâmetro 12 F foi obtido no ensaio biaxial de compressão de forma direta. Para as espécies de madeira Pinus elliottii e Goupia glabra (Cupiúba), obtiveram-se valores experimentais satisfatórios, sendo algumas inconsistências observadas em função da heterogeneidade do material. / Abstract: The completion of the uniaxial and biaxial tests permits a better understanding of the mechanical behavior of a material that has main failure directions and it is undoubtedly a method that researchers identified to achieve consistent results with the actual situation that a particular structure presents. This study aimed at studying the strength criterion proposed by Tsai and Wu, performing uniaxial and biaxial tests. The evaluation of this criterion was restricted to compression biaxial tests due to the difficulties presented by tension biaxial tests. With a compression biaxial test, the stresses in two main directions were simultaneously carried out, using a standard equipment test for one direction and for the perpendicular direction an equipment type pliers especially developed for this purpose. The failure parameter studied was 12 F , which evaluates the possibility of failure surface to be opened or closed, also considering that for the safety of design it is essential to obtain a closed surface for the failure criterion adopted. Furthermore, it was noted that in the compression biaxial test the parameter 12 F was obtained directly. For the species of wood Pinus elliottii and Goupia glabra (Cupiúba), the experimental values obtained were satisfactory with some inconsistencies observed in the light of the heterogeneity of the material. / Mestrado / Estruturas / Mestre em Engenharia Civil

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/257676
Date12 August 2018
CreatorsTodeschini, Rodrigo
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Mascia, Nilson Tadeu, 1956-, Lahr, Francisco Antonio Rocco, Jacintho, Ana Elisabete Paganelli Guimarães de Avila
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Civil, Arquitetura e Urbanismo, Programa de Pós-Graduação em Engenharia Civil
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format143 p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0026 seconds