Orientadores: Simonides Consani, Regina Maria Puppin Rontani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-14T12:05:44Z (GMT). No. of bitstreams: 1
Garcia_LucasdaFonsecaRoberti_D.pdf: 2236392 bytes, checksum: 81c798a6c0a3550904a44b971bdeaf20 (MD5)
Previous issue date: 2009 / Resumo: A grande quantidade de matizes que os compósitos possuem permite ao dentista obter excelentes resultados estéticos na confecção de uma restauração. Porém, para a confecção desta restauração, pouco material é utilizado e, muitas vezes, devido ao uso não freqüente, o compósito atinge o prazo de validade e a embalagem ainda contém material. O objetivo neste estudo foi avaliar a influência do Envelhecimento Artificial Acelerado (EAA - Sistema C-UV, Comexim) sobre a similaridade e a estabilidade de cor (?E), a opacidade (?OP) e a conversão monomérica de compósitos (Tetric Ceram, Tetric Ceram HB e Tetric Flow - Ivoclar/Vivadent) com prazo de validade vencido por 180 dias, comparando com àqueles com validade em vigência. Para avaliação das propriedades ópticas foram confeccionados 15 corpos-de-prova (n=5) em matriz de teflon, com 2 mm de espessura por 14 mm de diâmetro. Depois do polimento com discos Sof-Lex (3M Dental Products) foram submetidos às leituras de cor e opacidade (Espectrofotômetro PCB 6087 BYK GARDNER), antes e depois do EAA por 384 horas. Os valores obtidos para similaridade foram submetidos à análise estatística (t Student, p<0,05) e demonstraram que todos os compósitos antes do EAA apresentaram diferença significante para todas as coordenadas com exceção do Tetric Flow para a* e Tetric Ceram HB para b* antes do EAA. Após o EAA, somente o Tetric Ceram apresentou diferença significante para as coordenadas a* e b*. Os valores para ?E e ?OP foram submetidos à ANOVA 2 fatores e teste de Bonferroni (p<0,05) e demonstraram que todos os compósitos apresentaram alteração de cor acima do clinicamente aceitável (?E = 3,3). Somente o Tetric Flow apresentou diferença estatisticamente significante quando os prazos de validade foram comparados (p<0,05). Todos os compósitos avaliados apresentaram aumento nos valores numéricos de ?OP após o EAA, independente do prazo de validade, mas sem diferença significante (p>0,05). Para avaliação da conversão monomérica, 6 corpos-de-prova, sendo 3 envelhecidos e 3 não envelhecidos de cada compósito foram submetidos à verificação da densidade de ligações cruzadas (DLC) (Shimadzu HMV-2 Series) e do grau de conversão (GC) (FTIR - Thermo Scientific). Os valores obtidos foram submetidos à ANOVA 2 fatores e teste de Bonferroni (p<0,05) e demonstraram que todos os compósitos apresentaram diminuição na DLC após o EAA, independente do prazo de validade. Para o GC, o Tetric Flow vencido antes do EAA apresentou a maior porcentagem (71,42%), porém, sem diferença significante em relação aos demais compósitos (p>0,05). Concluiu-se que o prazo de validade e o EAA exerceram influência sobre as propriedades estudadas dos compósitos. / Abstract: Presently, the excellent aesthetic results obtained with composites require the dentist to use several composite resin hues to make a restoration. Nonetheless, to do this, little material is used, and many times, due to this low usage, the composite reaches its expiration date with material remaining in the packaging. The purpose of this study was to evaluate the influence of Artificial Accelerated Aging (AAA - Sistema C-UV, Comexim) on similarity and color stability (?E), opacity (?OP), and monomeric conversion of composites (Tetric Ceram, Tetric Ceram HB and Tetric Flow - Ivoclar/Vivadent) with their validity date expired for 180 days, comparatively to those within their validity date. For optical properties evaluation, 15 samples (n=5) with 2 mm of thick X 14 mm in diameter were made in a Teflon matrix. After polishing with Sof-Lex discs (3M Dental Products), they were submitted to color and opacity readings (Spectrophotometer PCB 6087 BYK GARDNER), before and after AAA for 384 hours. The values obtained for similarity were submitted to statistical analysis (t Student, p<0.05) and showed that all composites presented statistical significant difference for all coordinates, except Tetric Flow for a* and Tetric Ceram HB for b* before AAA. After AAA, only Tetric Ceram presented statistical significant difference for a* and b*. The values of ?E and ?OP were submitted to 2 way-ANOVA and Bonferroni's test (p<0.05) and showed that all composites presented color alteration above of the clinically acceptable (?E = 3.3). Only Tetric Flow presented statistical significant difference when the validity dates were compared (p<0.05). All studied composites showed increase in the values of ?OP after AAA, irrespective of the validity date, but without significant difference (p>0.05). To monomeric conversion evaluation, 6 samples, being 3 before aging and 3 after aging, of each composite, were submitted to cross-links density (CLD) (Shimadzu HMV-2 Series) and conversion degree evaluation (CD) (FTIR - Thermo Scientific). The values obtained were submitted to 2 way-ANOVA and Bonferroni's test (p<0.05) and showed that all composites presented decrease in CLD after AAA, irrespective of the validity date. For CD, Tetric Flow with expired date before AAA, showed the highest value (71.42%), however, without significant difference (p>0.05). It was concluded that the validity date and the AAA exert influence on the studied properties of the composites. / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290127 |
Date | 14 August 2018 |
Creators | Garcia, Lucas da Fonseca Roberti |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Puppin-Rontani, Regina Maria, 1959-, Consani, Simonides, 1939-, Souza, Fernanda de Carvalho Ranzeri Pires de, Cardoso, Paulo Eduardo Capel, Mesquita, Marcelo Ferraz, Guiraldo, Ricardo Danil |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 124 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds