The present thesis is focused on the study of Organic Semiconducting Single Crystals (OSSCs) and crystalline thin films. In particular solution-grown OSSC, e.g. 4-hdroxycyanobenzene (4HCB) have been characterized in view of their applications as novel sensors of X-rays, gamma-rays, alpha particles radiations and chemical sensors.
In the field of ionizing radiation detection, organic semiconductors have been proposed so far mainly as indirect detectors, i.e. as scintillators or as photodiodes.
I first study the performance of 4HCB single crystals as direct X-ray detector i.e. the direct photon conversion into an electrical signal, assessing that they can operate at room temperature and in atmosphere, showing a stable and linear response with increasing dose rate.
A dedicated study of the collecting electrodes geometry, crystal thickness and interaction volume allowed us to maximize the charge collection efficiency and sensitivity, thus assessing how OSSCs perform at low operating voltages and offer a great potential in the development of novel ionizing radiation sensors.
To better understand the processes generating the observed X-ray signal, a comparative study is presented on OSSCs based on several small-molecules: 1,5-dinitronaphthalene (DNN), 1,8-naphthaleneimide (NTI), Rubrene and TIPS-pentacene.
In addition, the proof of principle of gamma-rays and alpha particles has been assessed for 4HCB single crystals.
I have also carried out an investigation of the electrical response of OSSCs exposed to vapour of volatile molecules, polar and non-polar.
The last chapter deals with rubrene, the highest performing molecular crystals for electronic applications. We present an investigation on high quality, millimeter-sized, crystalline thin films (10 – 100 nm thick) realized by exploiting organic molecular beam epitaxy on water-soluble substrates. Space-Charge-Limited Current (SCLC) and photocurrent spectroscopy measurements have been carried out. A thin film transistor was fabricated onto a Cytop® dielectric layer. The FET mobility exceeding 2 cm2/Vs, definitely assess the quality of RUB films.
| Identifer | oai:union.ndltd.org:unibo.it/oai:amsdottorato.cib.unibo.it:6769 |
| Date | January 1900 |
| Creators | Ciavatti, Andrea <1986> |
| Contributors | Fraboni, Beatrice |
| Publisher | Alma Mater Studiorum - Università di Bologna |
| Source Sets | Università di Bologna |
| Language | English |
| Detected Language | English |
| Type | Doctoral Thesis, PeerReviewed |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/embargoedAccess |
Page generated in 0.0016 seconds