Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2015. / Made available in DSpace on 2016-10-19T12:58:51Z (GMT). No. of bitstreams: 1
338914.pdf: 2554765 bytes, checksum: 59d638f77c12b827fab82f56ff43850e (MD5)
Previous issue date: 2015 / Uma liga memória de forma Ti50Ni25Fe25 foi produzida por moagem mecânica. Suas propriedades estruturais, térmicas e magnética foram estudadas usando as técnicas difração de raios X (DRX), microscopia eletrônica de varredura (MEV), calorimetria diferencial de varredura (DSC - differential scanning calorimetry), espectroscopia de absorção fotoacústica, magnetometria de amostra vibrante (VSM - vibrating sample magnetometry) e espectroscopia Mössbauer (ME ? Mössbauer spectroscopy). Após 8 horas de moagem, o difratograma de DRX mostrou a nucleação da fase nanométrica Ti50Ni25Fe25 (B2) e uma fase amorfa (em pequena fração volumétrica), a qual foi confirmada por medidas de DSC. A curva de histerese medida por VSM e os espectros Mössbauer medidos em baixas temperaturas mostraram que a liga Ti50Ni25Fe25 (B2) possui características típicas de materiais ferromagnéticos moles. Os efeitos da alta pressão sobre a estabilidade estrutural da liga Ti50Ni25Fe25 (B2) foram estudados usando a técnica de difração de raios X por dispersão angular. Os difratogramas em função da pressão foram registrados à temperatura ambiente. Para pressões desde a pressão atmosférica até 7,0 GPa, os difratogramas mostraram a fase B2 (c.c.c.) e Ni elementar e/ou de uma solução sólida (SS)-(Fe,Ni). Para pressões entre 7,0 e 9,0 GPa, foi observada a transformação martensítica da estrutura B2 em uma B19 (de estrutura trigonal-hexagonal), bem como o desaparecimento da fase correspondente ao Ni elementar e/ou SS-(Fe,Ni). Além disso, observou-se a nucleação da fase FeNi3. As fases B19 e FeNi3 permaneceram até a mais elevada pressão utilizada (18,0 GPa). Os espectros ME em função da temperatura corroboraram os difratogramas ADXRD registrados uma função da pressão. Durante a descompressão, a transformação estrutural inversa B19 ? B2 foi observada em torno de 5,0 GPa, bem como o desaparecimento da fase FeNi3. Simulações dos espectros ME registrados em função de baixas temperaturas usando o método de distribuição do campo revelaram valores de campos magnéticos hiperfinos muito baixos para a faixa de temperatura utilizada. Além disso, observou-se um aumento gradual da ordem ferromagnética da liga com a diminuição da temperatura até a menor temperatura utilizada (15 K).<br> / Abstract : A shape memory Ti50Ni25Fe25 alloy was produced by mechanical alloying technique. Its structural, thermal and magnetic properties were studied by the X-ray diffraction (XRD), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), photoacoustic absorption spectroscopy (PAS), vibrating sample magnetometry (VSM) and Mössbauer spectroscopy (ME) techniques. After 8 h of milling, XRD pattern showed the formation of the nanostructured Ti50Ni25Fe25 (B2) and amorphous phases. The latter was confirmed by DSC measurements. VSM and ME measurements showed that the Ti50Ni25Fe25 alloy has a soft ferromagnetic behavior. High-pressure effect on its structural stability was studied using Angle-dispersive X-ray diffraction (ADXRD) measurements at the room temperature. From atmospheric pressure up to 7 GPa, the ADXRD patterns showed the B2 (b.c.c) phase and elemental Ni and/or a solid solution (SS)-(Fe,Ni). For pressures between 7.0 and 9.0 GPa, it was observed the martensitic phase transformation of B2 structure into a trigonal/hexagonal (B19) structure and the disappearance of elemental Ni and/or SS- (Fe, Ni) phase. Also, the nucleation of the FeNi3 phase was observed. The B19 and FeNi3 phases remain up to the highest pressure used (18 GPa). ME spectra as a function of temperature corroborated the recorded ADXRD patterns as a function of pressure. During decompression, the reverse structural B19? B2 transformation was observed at about 5.0 GPa as well as the disappearance of FeNi3. Simulation of the recorded ME spectra as a function of low temperatures using field distribution revealed very low hyperfine magnetic field values throughout the temperature range used. Also, it was observed a gradual increase in the ferromagnetic order alloy with decreasing temperature up to the lowest used temperature (15 K).
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/169474 |
| Date | January 2015 |
| Creators | Ferreira, Ailton da Silva |
| Contributors | Universidade Federal de Santa Catarina, Lima, João Cardoso de |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 115 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0102 seconds