Orientador: Marcelo Giannini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T14:52:05Z (GMT). No. of bitstreams: 1
Pacheco_RafaelRocha_M.pdf: 2265970 bytes, checksum: 2ea85fa1c09029765d270c2e28f5ebf7 (MD5)
Previous issue date: 2013 / Resumo: O objetivo do estudo foi avaliar o comportamento da luz, em diferentes comprimentos de onda, através de materiais restauradores indiretos com diferentes espessuras. A análise da passagem de luz foi realizada, através de quatro materiais restauradores odontológicos confeccionados pela técnica do CAD/CAM: uma resina composta indireta (RC) (Lava Ultimate, 3M ESPE), uma cerâmica feldspática (CF) (VitaBlocs, VITA) e duas cerâmicas à base de zircônia (ZK) (Katana, Noritake) e (ZL) (Lava, 3M ESPE). A perda total de irradiância, assim como a perda de energia em comprimentos de onda específicos (azul e violeta) foram analisados. As amostras sinterizadas tinham as dimensões de 20x20 mm, com variação na espessura: 0,5 mm, 1,0 mm, 1,5 mm e 2,0 mm (n=5). Uma fonte de luz de arco de plasma de alta potência com amplo espectro de luz foi utilizada (Arc Light II, Air Technologies). A caracterização dessa fonte de luz foi realizada através da avaliação da irradiância (mW/cm2), determinação dos espectros emitidos pela fonte de luz e padrão de saída pela ponta do aparelho. Para avaliar a quantidade de luz que passa através do material foi utilizado um espectroradiômetro (DAS 2100, Labsphere Inc.). Os corpos de prova foram posicionados sobre a superfície de uma lamínula de vidro que estava localizada na esfera integradora. O aparelho fotoativador foi posicionado de forma que a ponta do aparelho tocasse levemente e paralelo à superfície da amostra. Os dados foram tabulados e submetidos à análise estatística (análise de variância de dois fatores e teste de Tukey (?=0,05)). A interposição do material restaurador com 0,5 mm de espessura provocou uma perda de energia por volta de 60% e o aumento da espessura do material provocou redução da irradiância através dos mesmos. O material que apresentou menor perda de energia nas espessuras de 1,0 a 2,0 mm foi CF. A RC com espessura de 0,5 mm apresentou perda de energia de 56,2% e, com o aumento dessa espessura para 1,0 mm, essa perda de energia aumentou para 75,4%, semelhante à perda observada nas cerâmicas à base de zircônia. Os materiais RC, ZK e ZL apresentaram os maiores valores de perda de energia irradiante em até 1,0 mm de espessura. Com 1,5 mm e 2,0 mm, os materiais que apresentaram maior perda de energia foram: RC e ZK. Para todos os materiais, observou-se aumento significativo na perda de energia com o aumento da espessura do material e essa perda de energia foi dependente do tipo de material protético. A luz violeta (350 a 425 nm) apresentou menor capacidade de penetração quando comparada a luz azul para todas as espessuras e tipos de material restaurador indireto / Abstract: The aim of this study was to evaluate the light behavior, in different wavelengths, through different restorative materials with different thicknesses. The analysis was conducted using four dental restorative material obtained by the technique of CAD/CAM technology: an indirect composite resin (CR) (Ultimate Lava, 3M ESPE), a feldspathic ceramic (FC) (VITABLOCS, VITA) and two zirconia based ceramics (ZK) (Katana, Noritake) and (ZL) (Lava, 3M ESPE). The total loss of irradiance as well as the loss of energy at specific wavelengths (blue and violet) was analyzed. The sintered samples had dimensions of 20x20 mm, with a variation in thickness of 0.5 mm, 1.0 mm, 1.5 mm and 2.0 mm (n = 5). A plasma arc light source with high power and broad spectrum of light was used (Arc Light II, Air Technologies). The characterization of this light source was performed by evaluating the irradiance (mW/cm2), determining the spectra emitted by the light source and the output pattern on the tip of the device. To assess the amount of light passing through the material a spectroradiometer was used (DAS 2100, Labsphere Inc.). The specimens were placed on the surface of a thin glass (0.1 mm) located on the opening of the integrated sphere. The tip of the curing unit was positioned in parallel and lightly touching the sample surface. Data were tabulated and subjected to statistical analysis (two way ANOVA and Tukey test (? = 0.05)). The interposition of a restorative material of 0.5 mm thickness caused a loss of energy of approximately 60% and with the increase of the material thickness there was a reduction of the irradiance. The material that showed less energy loss in thickness from 1.0 to 2.0 mm was FC. CR with a thickness of 0.5 mm showed energy loss of 56.2%, and with 1.0 mm, this energy loss increased to 75.4%, similar to the loss observed in zirconia based ceramics. CR, ZK and ZL showed the highest values of radiant energy loss by up to 1.0 mm thick. With 1.5 mm and 2.0 mm, the materials with higher energy loss were: CR and ZK. For all materials, there was a significant increase in energy loss by increasing the thickness of the material and that energy loss is dependent on the type of indirect material. The violet light (350-425 nm) showed lower penetration capability compared to blue light for all thicknesses and types of indirect restorative material / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/287804 |
| Date | 03 January 2013 |
| Creators | Pacheco, Rafael Rocha, 1987- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Giannini, Marcelo, 1969-, Braga, Roberto Ruggiero, Silva, Alan Roger dos Santos |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 74 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds