Previous issue date: 2003 / Resumo: O objetivo deste trabalho foi verificar a influência da fonte de calor na fusibilidade e dureza de uma liga comercial à base de Ni-Cr (VERA BOND 11) nova, refundida (100%) e nova acrescida de sobras (50%). Para análise da fusibilidade foram confeccionadas 10 amostras para cada condição de liga, com uma tela para peneira de poliéster, com 11 X 11 filamentos de 0,22 mm de espessura, perfazendo uma malha de 100 espaços quadrados fixada bilateralmente por toda a extensão em fios de cera de 2,5 mm, contendo um pino formador do canal de alimentação no vértice. Para análise da dureza foram confeccionadas pastilhas em cera azul regular, com 8,0 mm de diâmetro por 2,0 mm de espessura, unidas a um pino formador do canal de alimentação. Após a obtenção dos padrões, estes foram fixados à base formadora do cadinho, de forma que a distância da base à câmara de reserva fosse 0,5 cm. Uma solução redutora da tensão de superfície foi aplicada sobre o padrão e após a secagem, este foi incluído em revestimento fosfatado - Termocast (Polidental, São Paulo Brasil) manipulado a vácuo, seguindo as instruções do fabricante quanto a proporção e tempo de manipulação. Os anéis foram aquecidos em forno elétrico (EDG) até atingirem a temperatura de 900°C, quando foram preenchidos por aproximadamente 15 gramas de liga fundida pela fonte de calor maçarico oxigênio/acetileno ou indução. A injeção da liga foi realizada por uma máquina centrifuga. Após a obtenção e limpeza dos corpos-de-prova foi realizada a análise de fusibilidade, com o auxílio de um microscópio comparador com aumento de 16 X, considerando o número de espaços preenchidos no molde pela liga. Para análise da dureza superficial Rockwell 30T, os corpos-de-prova foram incluídos em resina acrílica quimicamente ativada, polidos e levados ao aparelho de dureza Testor HTI Super-Panambra, onde foram realizadas as medidas e obtidas as médias. Os resultados foram submetidos à análise de variância e as médias comparadas pelo teste de Tukey, em nível de significância de 5%. Quando foram comparadas as fontes de calor com os diferentes tipos de liga houve diferença estatística significativa entre as fontes de calor, na qual o aquecimento por indução demonstrou melhores resultados para fusibilidade. Não houve diferença estatística significativa nos valores médios de dureza quando foi utilizada a fonte de calor maçarico e aquecimento por indução para as ligas virgem e mista, porém o aquecimento por indução demonstrou melhores resultados que o maçarico, diferindo estatisticamente os valores de dureza, quando da utilização da liga refundida / Abstract: The aim of the present study was to verify the influence of the heat source on the castability and hardness of a Ni-Cr-based commercial alloy ¿ VERA BOND 11 - in three different conditions: new (first use), recast, and new mixed with scraps. In order to evaluate castability, 10 specimens were made for each alloy condition, using a polyester sieve with 11x11 filaments, 0.22mm thick, resulting in a screen with 100 square spaces. This screen was fixed to 0.25mm threads along the extension of two sides, and a post was fixed to its vertex. In order to perform hardness analysis, circular specimens made of regular blue wax measuring 8.0 mm in diameter and 2.0 mm thick were connected to the post, forming the sprue. The patterns were then fixed to the casting chamber, so that the distance from the base to the reservoir was 0.5 cm. A surface tension-reducing solution was abundantly applied to the patterns and after drying, the patterns were embedded into a phosphate-bonded investment - Termocast (Polidental, São Paulo, Brazil) manipulated under vacuum pressure, following manufacturer's instructions regarding proportions and manipulation times. Casting rings were placed in an electric oven (Bravac) until the temperature of 900°C was reached, and were then filled with approximately 15 grams of alloy, molten either by an oxigen/acethylen gas torch or by induction as heat sources. Following this procedure, castability analysis was performed. A comparison microscope of 16x magnifying power was used to count the number of spaces which were filled by the alloy. In order to evaluate hardness Rockwell 30T, specimens were embedded in chemically activated acrylic resin and then placed on a Testor HTI Super-Panambra hardness teste r. Hardness values for each specimen were obtained, and the average hardness was calculated. Results were submitted to analysis of variance and averages were compared by Tukey's test at 5% probability. There were statistically significant differences between the heat sources applied to the different types of alloy, with induction presenting the best castability results. There were no statistically significant differences in the average hardness values between torch or induction as the heating source for new and mixed alloys, although induction showed the best results, leading to statistically significant differences in hardness, when recast alloy was used. / Mestrado / Mestre em Materiais Dentários
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290116 |
Date | 24 April 2003 |
Creators | Fernandes, Daniela Rodrigues |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Panzeri, Fernanda de Carvalho, Correr Sobrinho, Lourenço |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 76f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0014 seconds