Orientador : Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T10:08:15Z (GMT). No. of bitstreams: 1
Belloti_HaglayPalandideOliveira_D.pdf: 2400768 bytes, checksum: acd420fb3abb38a2f971df034c8de401 (MD5)
Previous issue date: 2002 / Resumo: O propósito deste estudo foi avaliar o efeito do tempo de armazenagem (24 horas e 6 meses) na resistência à remoção por tração de coroas totais metálicas fixadas com 3 tipos de cimento dental. Noventa incisivos bovinos foram fixados pelas raízes em resina epóxica. As porções coronárias foram preparadas para receber coroas totais completas, usando pontas diamantadas n° 4103 com paredes axiais com expulsividade de 10° e término cervical em ombro reto. Noventa coroas totais foram fundidas com a liga de níquel-cromo (Verabond 2). Após a limpeza e jateamento com óxido de alumínio (50 /lm) as coroas foram separadas em 3 grupos de 30 amostras. Em seguida, trinta coroas foram fixadas com cimento de fosfato de zinco (55 White), 30 com cimento de ionõmero de vidro modificado por resina (Fuji Plus) e 30 com cimento resinoso (Rely X). As coroas foram fixadas com auxílio de prensa pneumática, com carga estática de 9 kg por 1O minutos. Após, todos os corpos-de-prova foram armazenados em água destilada numa estufa a 37° C, sendo que 15 corpos-de-prova para cada agente de fixação foram armazenados por 24 horas e 15 por 6 meses. Após os períodos de armazenagem, os corpos-de-prova foram submetidos ao ensaio de resistência à remoção por tração numa máquina de ensaio universal Instron à velocidade de 1 mmlminuto. Os resultados foram submetidos à análise de variância e às médias ao teste de Tukey (p<0,05) e mostraram que as coroas fixadas com o cimento resinoso apresentou valores de resistência à remoção por tração superiores nos tempos de armazenagem de 24 horas e 6 meses em relação ao cimento de ionõmero de vidro e fosfato de zinco (p<0,05). Os valores de resistência à remoção por tração no tempo de armazenagem de 6 meses foram superiores ao de 24 horas para os cimentos resinoso e ionõmero de vidro. Nenhuma diferença estatística foi observada para o cimento de fosfato de zinco / Abstract: The purpose of this study was to evaluate the effect of storage time (24 hours and 6 month) in the tensile strength of complete cast crowns luted with 3 kinds of dental cements. Ninety bovin incisors were embedded in epoxic resin. The coronal portions of the teeth were prepared to receive complete crowns using a 4103 diamond bur under refrigeration with 100 of tapering and right shoulder. Ninety crowns were cast with nickel-chromium (Verabond 2) melted by gas-oxygen torch. After the crowns were cleaned and blasted with aluminum oxide (50 _m) and they were separated in three groups of thirty specimens each one. Afterwards thirty crowns were luted with zinc phosphate cement (SSWhite), Thirty luted with resin modified glass ionomer cement (Fuji Plus) and thirty with resin cement (Rely X). The crowns were luted onto the tooth with static load of 9 kg for 10 minutes. After ali specimens were stored in distilled water 370 C, where 15 specimens for each cement were storage for 24 hours and 15 for 6 months. Afterwards the storage time, the specimens were submitled to the tension tests on Instron machine with a speed of 1mmlmin. The results were analyzed by ANOVA and Tukey's test (p<0.05) and showed that the crowns luted with resin cement showed higher values tension strength in the storage time of the 24 hours and 6 months in relation of the glass ionomer cement and zinc phosphate (p<0.05). The values of the tension strength of the 6 months storage was higher than 24 hours for the resin cement and glass ionomer cement. No statistic difference was found for the zinc phosphate cement / Doutorado / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289583 |
| Date | 18 November 2002 |
| Creators | Belloti, Haglay Palandi de Oliveira |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Correr Sobrinho, Lourenço, 1960-, Vilella, Lauro Caardoso, Boscariolli, Ana Paula Teixeira, Consani, Simonides |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 82f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds