Previous issue date: 1991 / Resumo: O propósito deste trabalho foi verificar a influência da intensidade luminosa emitida pelas cunhas refletoras, no grau de dureza dos compósitos odontológicos. Foram utilizados dois compósitos para uso em restaurações de dentes posteriores (Herculite XR e P-50), e confeccionadas trinta amostras de cada material, usando a emissão da luz visivel diretamente sobre o compósito, ou através de uma cunha refletora (HAWE NEOS), em tempos determinados de 30, 60, 90, 120, 150 e 180 segundos, para cada cinco amostras, respectivamente. Após o processo de polimerização, as amostras foram incluidas em resina à base de poliéster, e polidas. A seguir, as amostras foram divididas em duas regiões: superficie e fundo, onde foram feitas quatro penetrações em cada região, e as medidas de dureza foram obtidas utilizando-se um aparelho Durimet (Leitz Wetzlar), equipado com diamante Knoop, com carga de 50 gramas e tempo de 30 segundos para cada penetração. Os resultados indicaram superioridade estatistica ao nível de 5% de probabilidade do compósito P-50, independente do uso de cunhas refletoras, em relação ao Herculite XR nas regiões de superficie e fundo das amostras, em todos os tempos considerados. Observou-se que, usando cunhas refletoras, os valores de dureza foram estatisticamente inferiores ao nivel de 5% de probabilidade, na região de superfície e de fundo do compósito Herculite XR, mas sem diferença estatística na região de superficie do compósito P-50, a partir de 150 segundos de exposição à luz visivel / Abstract: The purpose of this paper was to investigate the influence of light intensity by reflecting light wedges in hardness from dental composites. Two visible light activated composites were used in posterior teeth restoration (Herculite XR and P-50) and were fabricated thirty samples of each material using visible light emission, directly on the composite or through reflecting light wedges (HAWE NEOS), in previous time determination of 30, 60, 90, 120, 150 and 180 seconds, for each of the five samples, respes tively. After the polymerization procedure, the samples were in serted in polyester resin based, then polished. Following, the samples were divided into two regions: surface and bottom, where four indentations were made in each region, and the hardness meas urements were obtained using Durimet device (Leitz Wetzlar), provided with a Knoop diamond, charged of 50 grams in 30 seconds of time for each indentation. The results showed that there is statistical superiority at 5% probability from the composite P-50, regardless the reflecting light wedges usage, related to Herculite XR in surface and bottom of samples in all the previous time considered. It was no ticed, yet, that the usage of reflecting light wedges, the values for hardness were statistically inferior at 5% probability level, in both regions: surface and bottom of Herculite XR composite; but no statistical ditference at P-50 composite surface region, from 150 seconds at visible light exposure / Mestrado / Materiais Dentarios / Mestre em Odontologia
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288169 |
Date | 13 July 2018 |
Creators | Dall'Magro, Eduardo |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Goes, Mario Fernando de, 1954- |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | [97]f. : il., application/octet-stream |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0015 seconds