Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-11T14:14:43Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_MaterialCompositoMatriz.pdf: 3287134 bytes, checksum: 7b7c1ee635985a997b7df99e008cd690 (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-23T12:34:35Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_MaterialCompositoMatriz.pdf: 3287134 bytes, checksum: 7b7c1ee635985a997b7df99e008cd690 (MD5) / Made available in DSpace on 2014-06-23T12:34:35Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_MaterialCompositoMatriz.pdf: 3287134 bytes, checksum: 7b7c1ee635985a997b7df99e008cd690 (MD5)
Previous issue date: 2010 / Este estudo propõe avaliar o comportamento mecânico dos compósitos de matriz cimentícia reforçados com fibras de sisal e malva. Correlacionar o comportamento dos materiais com variação do tipo e do comprimento das fibras. O material base utilizado na fabricação do compósito foi cimento, areia, água e fibra de sisal e malva. Usou-se u traço 1 : 2 : 0,5 (cimento, areia e água), com adição de 1% de fibras em
relação ao peso da mistura. As fibras foram previamente cortadas no comprimento
de 15 mm e 25 mm e adicionadas manualmente à mistura. As correlações dos
compósitos foram obtidos através do ensaio de flexão em três pontos, seguindo
norma RILEM 49. As características micro-estruturais foram avaliadas através do
uso do microscópio eletrônico de varredura.Os resultados obtidos indicam que a
inserção de fibras na matriz cimentícia diminui a força máxima aplicada no corpo de
prova, porém houve um ganho na tenacidade e na pseudo ductilidade do material
após o aparecimento da 1ª trinca. As fibras mais longas mostraram melhor
desempenho com um pequeno destaque às fibras de MALVA. / The purpose of this thesis is evaluate the mechanical behavior of cementitious matrix
composites reinforced with sisal fibers and mauve, and correlate the material’s
behavior with variations in the fibers types and lengths. The base material used in the
manufacture of the composite was cement, sand, water and sisal fibers and mauve.
It was used the trace 1: 2: 0,5 (cement, sand and water, respectively), with the
addition of 1% in mass of fibers. The fibers had been previously cut in the length of
15mm e 25mm and manually added to the mix. The correlations of the composites
were obtained by bending tests in three points, following the RILEM 49 norm. The
micro-structural characteristics were evaluated with electron microscopy. The results
show that the insertion of fibers in the cementitious matrix reduces the maximum
force applied to the specimen, even tough there was an increase in the material
toughness and pseudo-ductility after the appearance of the first fissure. The longest
fibers demonstrated better performance with a small highlight on the mauve fibers.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/5111 |
| Date | 22 December 2010 |
| Creators | MARTINS NETO, Sandoval Ferreira |
| Contributors | FUJIYAMA, Roberto Tetsuo |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia Mecânica, UFPA, Brasil, Instituto de Tecnologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds