Response and failure analysis of a graphite-epoxy laminate containing terminating internal plies

A change in laminate thickness due to terminating internal plies acts as a stress riser for both intralamina and interlaminar stresses. This laminate configuration is referred to as a ply drop. The linear elastic, three-dimensional stress distributions in the vicinity of a ply drop are determined for a graphite-epoxy laminate subject to axial tension and compression by a finite element analysis. It is shown that the interlaminar stresses have a maximum magnitude at the ply drop-off, and decrease proceeding away from the drop-off. Two modes of failure initiation are analyzed. In the pure resin regions surrounding the dropped plies, the maximum stress criterion is assumed to govern failure. The Tsai-Wu criterion is used for intralamina failure prediction. The influence of two laminate lay-ups and a variety of ply drop geometries on the response and failure are presented. / M.S.

Identiferoai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/91127
Date January 1985
CreatorsKemp, Brian Lee
ContributorsAerospace and Ocean Engineering
PublisherVirginia Polytechnic Institute and State University
Source SetsVirginia Tech Theses and Dissertation
Languageen_US
Detected LanguageEnglish
TypeThesis, Text
Formatv, 70 leaves, application/pdf, application/pdf
RightsIn Copyright, http://rightsstatements.org/vocab/InC/1.0/
RelationOCLC# 13131190

Page generated in 0.0019 seconds